The gas induced semi-solid(GISS) is a rheocasting process that produces semi-solid slurry by applying fine gas bubble injection through a graphite diffuser.The process is developed to be used in the die casting indust...The gas induced semi-solid(GISS) is a rheocasting process that produces semi-solid slurry by applying fine gas bubble injection through a graphite diffuser.The process is developed to be used in the die casting industry.To apply the GISS process with a die casting process,a GISS maker unit is designed and attached to a conventional die casting machine with little modifications.The commercial parts are developed and produced by the GISS die casting process.The GISS die casting shows the feasibility to produce industrial parts with aluminum 7075 and A356 with lower porosity than liquid die casting.展开更多
Vacuum die casting can reduce the'air entrapment'phenomenon during casting process.Based on the temperature measurements at metal-die interface with different processing parameters,such as slow shot speed(VL),...Vacuum die casting can reduce the'air entrapment'phenomenon during casting process.Based on the temperature measurements at metal-die interface with different processing parameters,such as slow shot speed(VL),high shot speed(VH),pouring temperature(Tp)and initial die temperature(Tm),inverse method was developed to determine the interfacial heat transfer coefficient(IHTC).The results indicate that a closer contact between the casting and die could be achieved when the vacuum system is used.It is found that the vacuum could strongly increase the values of IHTC and decrease the grain size in castings.The IHTC could have a higher peak value with increasing the Tp from680to720℃or the VL from0.1to0.4m/s.In addition,the influence of the VH and Tm on IHTC could be negligible.展开更多
Heat transfer at the metal-die interface has a great influence on the solidification process and casting structure. As thin-wall components are extensively produced by high pressure die casting process(HPDC), the B390...Heat transfer at the metal-die interface has a great influence on the solidification process and casting structure. As thin-wall components are extensively produced by high pressure die casting process(HPDC), the B390 alloy finger-plate casting was cast against an H13 steel die on a cold-chamber HPDC machine. The interfacial heat transfer behavior at different positions of the die was carefully studied using an inverse approach based on the temperature measurements inside the die. Furthermore, the filling process and the solidification rate in different finger-plates were also given to explain the distribution of interfacial heat flux(q) and interfacial heat transfer coefficient(h). Measurement results at the side of sprue indicates that qmax and hmax could reach 9.2 MW·m^(-2) and 64.3 kW ·m^(-2)·K^(-1), respectively. The simulation of melt flow in the die reveals that the thinnest(T_1) finger plate could accelerate the melt flow from 50 m·s^(-1) to 110 m·s^(-1). Due to this high velocity, the interfacial heat flux at the end of T_1 could firstly reach a highest value 7.92 MW·m^(-2) among the ends of T_n(n=2,3,4,5). In addition, the q_(max) and h_(max) values of T_2, T_4 and T_5 finger-plates increase with the increasing thickness of the finger plate. Finally, at the rapid decreasing stage of interfacial heat transfer coefficient(h), the decreasing rate of h has an exponential relationship with the increasing rate of solid fraction(f).展开更多
Two kinds of bi-metal composite parts （Sn-15%Pb and Pb-22%Sn bi-metal system, and Al-7%Si and SiCp/6061 MMC bi-metal system） were prepared by the strain-induced melt activated thixo-forging. The interfaces of the bi...Two kinds of bi-metal composite parts （Sn-15%Pb and Pb-22%Sn bi-metal system, and Al-7%Si and SiCp/6061 MMC bi-metal system） were prepared by the strain-induced melt activated thixo-forging. The interfaces of the bi-metal composites were observed by OM and SEM. The observations show that the semisolid metals keep independence during thixo-forging. The solid phases in the semisolid slurries maintain their original morphologies after thixo-forging. The liquid phases near the interface mix together and form a thin layer. The interfaces are bonded firmly with the metallurgical bonding. No oxide layers are found at the interfaces. Strengths of the interfaces were investigated by the micro-hardness test. The experimental results show that the composite interfaces have high strength. However, the agglomerated enhancing particles cause fine defect on the interface of the Al-7%Si and SiCr/6061 MMC bi-metal composite.展开更多
基金supports from Prince of Songkla University (No.AGR530031M)the Royal Golden Jubilee Ph.D program (No.PHD/0173/2550)
文摘The gas induced semi-solid(GISS) is a rheocasting process that produces semi-solid slurry by applying fine gas bubble injection through a graphite diffuser.The process is developed to be used in the die casting industry.To apply the GISS process with a die casting process,a GISS maker unit is designed and attached to a conventional die casting machine with little modifications.The commercial parts are developed and produced by the GISS die casting process.The GISS die casting shows the feasibility to produce industrial parts with aluminum 7075 and A356 with lower porosity than liquid die casting.
基金Project (2016YFB0301001) supported by the National Key Research and Development Program of ChinaProject (2015M580093) supported by the General Financial Grant from the China Postdoctoral Science Foundation of China
文摘Vacuum die casting can reduce the'air entrapment'phenomenon during casting process.Based on the temperature measurements at metal-die interface with different processing parameters,such as slow shot speed(VL),high shot speed(VH),pouring temperature(Tp)and initial die temperature(Tm),inverse method was developed to determine the interfacial heat transfer coefficient(IHTC).The results indicate that a closer contact between the casting and die could be achieved when the vacuum system is used.It is found that the vacuum could strongly increase the values of IHTC and decrease the grain size in castings.The IHTC could have a higher peak value with increasing the Tp from680to720℃or the VL from0.1to0.4m/s.In addition,the influence of the VH and Tm on IHTC could be negligible.
基金financially supported by the class General Financial Grant from the China Postdoctoral Science Foundation(No.2015M580093)the National Nature Science Foundation of China(No.20151301587)the National Major Science and Technology Program of China(No.2012ZX04012011)
文摘Heat transfer at the metal-die interface has a great influence on the solidification process and casting structure. As thin-wall components are extensively produced by high pressure die casting process(HPDC), the B390 alloy finger-plate casting was cast against an H13 steel die on a cold-chamber HPDC machine. The interfacial heat transfer behavior at different positions of the die was carefully studied using an inverse approach based on the temperature measurements inside the die. Furthermore, the filling process and the solidification rate in different finger-plates were also given to explain the distribution of interfacial heat flux(q) and interfacial heat transfer coefficient(h). Measurement results at the side of sprue indicates that qmax and hmax could reach 9.2 MW·m^(-2) and 64.3 kW ·m^(-2)·K^(-1), respectively. The simulation of melt flow in the die reveals that the thinnest(T_1) finger plate could accelerate the melt flow from 50 m·s^(-1) to 110 m·s^(-1). Due to this high velocity, the interfacial heat flux at the end of T_1 could firstly reach a highest value 7.92 MW·m^(-2) among the ends of T_n(n=2,3,4,5). In addition, the q_(max) and h_(max) values of T_2, T_4 and T_5 finger-plates increase with the increasing thickness of the finger plate. Finally, at the rapid decreasing stage of interfacial heat transfer coefficient(h), the decreasing rate of h has an exponential relationship with the increasing rate of solid fraction(f).
基金Project(1343-71333000469) supported by the Funding of Graduate Student Training of Central South University,China
文摘Two kinds of bi-metal composite parts （Sn-15%Pb and Pb-22%Sn bi-metal system, and Al-7%Si and SiCp/6061 MMC bi-metal system） were prepared by the strain-induced melt activated thixo-forging. The interfaces of the bi-metal composites were observed by OM and SEM. The observations show that the semisolid metals keep independence during thixo-forging. The solid phases in the semisolid slurries maintain their original morphologies after thixo-forging. The liquid phases near the interface mix together and form a thin layer. The interfaces are bonded firmly with the metallurgical bonding. No oxide layers are found at the interfaces. Strengths of the interfaces were investigated by the micro-hardness test. The experimental results show that the composite interfaces have high strength. However, the agglomerated enhancing particles cause fine defect on the interface of the Al-7%Si and SiCr/6061 MMC bi-metal composite.