CeO2-TiO2 films and CeO2-TiO/SnO2：Sb （6 mol%） double films were deposited on glass substrates by radio-frequency magnetron sputtering （R.F. Sputtering）, using SnO2：Sb（6 mol%） target, and CeO2- TiO2 targets wit...CeO2-TiO2 films and CeO2-TiO/SnO2：Sb （6 mol%） double films were deposited on glass substrates by radio-frequency magnetron sputtering （R.F. Sputtering）, using SnO2：Sb（6 mol%） target, and CeO2- TiO2 targets with different molar ratio of CeO2 to TiO2 （CeO2：TiO2-0：1.0; 0.1：0.9; 0.2：0.8; 0.3：0.7; 0.4：0.6; 0.5：0.5; 0.6：0.4; 0.7：0.3; 0.8：0.2; 0.9：0.1; 1.0：0）. The films are characterized by UV-visible transmission and infrared reflection spectra, scanning electron microscopy （SEM）, Raman spectroscopy, X-ray photoelectron spectroscopy （XPS） and X-ray diffraction （XRD）, respectively. The obtained results show that the amorphous phases composed of CeO2-TiO2 play an important role in absorbing UV, there are Ce^3-, Ce^4- and Ti^4- on the surface of the films; the glass substrates coated with CeO2-TiO2 （Ce/Ti=0.5：0.5; 0.6：0.4）/SnO2：Sb（6 mol%） double films show high absorbing UV（〉99）, high visible light transmission （75%） and good infrared reflection （〉70%）. The sheet resistance of the films is 30-50 Ω/□. The glass substrates coated with the double functional films can be used as window glass of buildings, automobile and so on.展开更多
TiO2-CeO2 films were deposited on soda-lime glass substrates at varied substrate temperatures by rf magnetron sputtering using 40% molar TiO2-60% molar CeO2 ceramic target in Ar：O2=95：5 atmosphere.The structure,surf...TiO2-CeO2 films were deposited on soda-lime glass substrates at varied substrate temperatures by rf magnetron sputtering using 40% molar TiO2-60% molar CeO2 ceramic target in Ar：O2=95：5 atmosphere.The structure,surface composition,UV-visible spectra of the films were measured by scanning electron microscopy and X-ray diffraction,and X-ray photoelectron spectroscopy,respectively.The experimental results show that the films are amorphous,there are only Ti^4＋ and Ce^4＋ on the surface of the films,the obtained TiO2-CeO2 films shou a good uniformity and high densification,and the films deposited on the glass can shield ultraviolet light without significant absorpition of visible light,the films deposited on substrates at room temperature and 220℃ absorb UV effectively.展开更多
基金the program for Changjiang Scholars and Innovative Research Team in University (No.IRT0547
文摘CeO2-TiO2 films and CeO2-TiO/SnO2：Sb （6 mol%） double films were deposited on glass substrates by radio-frequency magnetron sputtering （R.F. Sputtering）, using SnO2：Sb（6 mol%） target, and CeO2- TiO2 targets with different molar ratio of CeO2 to TiO2 （CeO2：TiO2-0：1.0; 0.1：0.9; 0.2：0.8; 0.3：0.7; 0.4：0.6; 0.5：0.5; 0.6：0.4; 0.7：0.3; 0.8：0.2; 0.9：0.1; 1.0：0）. The films are characterized by UV-visible transmission and infrared reflection spectra, scanning electron microscopy （SEM）, Raman spectroscopy, X-ray photoelectron spectroscopy （XPS） and X-ray diffraction （XRD）, respectively. The obtained results show that the amorphous phases composed of CeO2-TiO2 play an important role in absorbing UV, there are Ce^3-, Ce^4- and Ti^4- on the surface of the films; the glass substrates coated with CeO2-TiO2 （Ce/Ti=0.5：0.5; 0.6：0.4）/SnO2：Sb（6 mol%） double films show high absorbing UV（〉99）, high visible light transmission （75%） and good infrared reflection （〉70%）. The sheet resistance of the films is 30-50 Ω/□. The glass substrates coated with the double functional films can be used as window glass of buildings, automobile and so on.
文摘TiO2-CeO2 films were deposited on soda-lime glass substrates at varied substrate temperatures by rf magnetron sputtering using 40% molar TiO2-60% molar CeO2 ceramic target in Ar：O2=95：5 atmosphere.The structure,surface composition,UV-visible spectra of the films were measured by scanning electron microscopy and X-ray diffraction,and X-ray photoelectron spectroscopy,respectively.The experimental results show that the films are amorphous,there are only Ti^4＋ and Ce^4＋ on the surface of the films,the obtained TiO2-CeO2 films shou a good uniformity and high densification,and the films deposited on the glass can shield ultraviolet light without significant absorpition of visible light,the films deposited on substrates at room temperature and 220℃ absorb UV effectively.