Li（Mn1/3Ni1/3Co1/3）O2 cathode materials were fabricated by a hydroxide precursor method. A1203 was coated on the surface of the Li（Mn1/3Ni1/3Co1/3）O2 through a simple and effective one-step electrostatic self-asse...Li（Mn1/3Ni1/3Co1/3）O2 cathode materials were fabricated by a hydroxide precursor method. A1203 was coated on the surface of the Li（Mn1/3Ni1/3Co1/3）O2 through a simple and effective one-step electrostatic self-assembly method. In the coating process, a NaHCO3- H2CO3 buffer was formed spontaneously when CO2 was introduced into the NaAlO2 solution. Compared with bare Li（Mn1/3Ni1/3Co1/3）O2, the surface-modified samples exhibited better cycling performance, rate capability and rate capability retention. The Al2O3-coated Li（Mn1/3Ni1/3Co1/3）O2 electrodes delivered a discharge capacity of about 115 mAh.g-1 at 2 A.g-1, but only 84 mAh.g-1 for the bare one. The capacity retention of the Al2O3-coated Li（Mn1/3Ni1/3Co1/3）O2 was 90.7% after 50 cycles, about 30% higher than that of the pristine one.展开更多
基金supported by the National Natural Science Foundation of China(21273222)
文摘Li（Mn1/3Ni1/3Co1/3）O2 cathode materials were fabricated by a hydroxide precursor method. A1203 was coated on the surface of the Li（Mn1/3Ni1/3Co1/3）O2 through a simple and effective one-step electrostatic self-assembly method. In the coating process, a NaHCO3- H2CO3 buffer was formed spontaneously when CO2 was introduced into the NaAlO2 solution. Compared with bare Li（Mn1/3Ni1/3Co1/3）O2, the surface-modified samples exhibited better cycling performance, rate capability and rate capability retention. The Al2O3-coated Li（Mn1/3Ni1/3Co1/3）O2 electrodes delivered a discharge capacity of about 115 mAh.g-1 at 2 A.g-1, but only 84 mAh.g-1 for the bare one. The capacity retention of the Al2O3-coated Li（Mn1/3Ni1/3Co1/3）O2 was 90.7% after 50 cycles, about 30% higher than that of the pristine one.