Niobium ion implantation is found to significantly decrease the friction coefficient and improve wear resistance of NiTi shape memory alloy. Scanning electron microscope（SEM） observations indicate that surface groov...Niobium ion implantation is found to significantly decrease the friction coefficient and improve wear resistance of NiTi shape memory alloy. Scanning electron microscope（SEM） observations indicate that surface grooves formed on NiTi during the mechanical polishing are removed after Nb ion implantation. Dry friction tests show that Nb implanted NiTi samples exhibit a lower friction coefficient, narrower wear tracks, fewer wear debris generated, 46 %-62 % reduction in wear width, and29 %-49 % reduction in wear depth compared with the untreated NiTi. Wear resistance is related to the incident parameters, and the Nb implanted NiTi with the incident dose of 2.5 9 1017ionsácm-2, and incident current of2 mA behaves the best wear performance. The lubricating of Nb2O5, good oxidation resistance of Nb in NiTi, and increased micro-hardness of NiTi are responsible for the enhanced wear resistance.展开更多
It is imperative to develop a novel matching of metallic substrate and self-lubricating coating for aircraft spherical plain bearing in a wide range of service conditions.As a new type of superelastic material,60NiTi ...It is imperative to develop a novel matching of metallic substrate and self-lubricating coating for aircraft spherical plain bearing in a wide range of service conditions.As a new type of superelastic material,60NiTi alloy meets the performance requirements of aerospace bearing materials,but exhibits poor tribological performance,especially under the conditions of dry sliding friction.A Hydrogenated Diamond-Like Carbon(H-DLC)coating was deposited on the 60NiTi alloy to improve its tribological performance.The microstructure and mechanical behavior of the 60NiTi alloy and its H-DLC coating were explored.Results show that improvement of friction and wear performance of the H-DLC coating deposited on the 60NiTi substrate is mainly achieved by graphitization at the friction interface and the transfer film produced on the counterpart ball.The increased friction load leads to intensification of graphitization at the friction interface and formation of continuous and compact transfer film on the surface of the counterpart ball.展开更多
Electrochemical tests and surface analysis were applied to study the corrosion behavior and passive film characteristics of three-dimensional-printed NiTi shape memory alloys fabricated by laser-powder bed fusion(LPBF...Electrochemical tests and surface analysis were applied to study the corrosion behavior and passive film characteristics of three-dimensional-printed NiTi shape memory alloys fabricated by laser-powder bed fusion(LPBF) in artificial saliva at 37.C. The passivity of L-PBF NiTi shows to be influenced by the process parameters and resulting morphological and physicochemical surface properties. The results show that the defects at the surface of L-PBF Ni Ti can promote the passivation rate in the early stages of exposure but a slowly formed passive film shows the best corrosion protection. The thickness of the passive film is positively correlated with its corrosion protective performance. The L-PBF NiTi alloy prepared at a linear energy density of 0.2 J·m^(-1) and volumetric energy density of 56 J·mm^(-3) shows the least defects and best corrosion protection. An outer Ti-rich and inner Ni-rich dense passive film could be also obtained showing higher corrosion resistance.展开更多
The microstructure,mechanical and micro/nano-tribological properties of the 60NiTi film annealed at different temperature were investigated.The results reveal that annealing as-deposited 60NiTi film at 300,375,and 600...The microstructure,mechanical and micro/nano-tribological properties of the 60NiTi film annealed at different temperature were investigated.The results reveal that annealing as-deposited 60NiTi film at 300,375,and 600℃ for 1 h leads to structural relaxation,partial crystallization and full crystallization,respectively.Compared with the structurally relaxed structure,the partially crystallized structure exhibits increased hardness but decreased elastic modulus.This is because that the elastic modulus is reduced by Voigt model while the hardness is improved by composite effect.Due to the highest hardness and ratio of hardness to elastic modulus(H/E),the partially crystallized 60NiTi film has the lowest penetration depth and residual depth(i.e.,groove depth).Besides,the results also reveal that ductile plowing is the dominant wear mechanism for all the annealed 60NiTi films.Under the condition of the ductile plowing,coefficient of friction and wear resistance are related to penetration depth and residual depth,respectively.Therefore,the partially crystallized 60NiTi film shows the best tribological performance at the micro/nano-scale.The current work not only highlights the important roles of hardness and H/E in improving the micro/nano-tribological properties but also concludes an efficient and simple method for simultaneously increasing hardness and H/E.展开更多
基金financially supported by the National Basic Research Program of China(No.2012CB619403)the National Natural Science Foundation of China(No.51171009)the Tan Chin-Tuan exchange fellowship funding in Nanyang Technological University
文摘Niobium ion implantation is found to significantly decrease the friction coefficient and improve wear resistance of NiTi shape memory alloy. Scanning electron microscope（SEM） observations indicate that surface grooves formed on NiTi during the mechanical polishing are removed after Nb ion implantation. Dry friction tests show that Nb implanted NiTi samples exhibit a lower friction coefficient, narrower wear tracks, fewer wear debris generated, 46 %-62 % reduction in wear width, and29 %-49 % reduction in wear depth compared with the untreated NiTi. Wear resistance is related to the incident parameters, and the Nb implanted NiTi with the incident dose of 2.5 9 1017ionsácm-2, and incident current of2 mA behaves the best wear performance. The lubricating of Nb2O5, good oxidation resistance of Nb in NiTi, and increased micro-hardness of NiTi are responsible for the enhanced wear resistance.
基金co-supported by the National Natural Science Foundation of China(No.51905466)the Aeronautical Science Foundation of China(No.201945099002)+1 种基金the Natural Science Foundation of Hebei Province,China(Nos.E2021203191 and E2020203184)the Youth Top Talent Project of Hebei Province Higher Education,China(No.BJ2019058).
文摘It is imperative to develop a novel matching of metallic substrate and self-lubricating coating for aircraft spherical plain bearing in a wide range of service conditions.As a new type of superelastic material,60NiTi alloy meets the performance requirements of aerospace bearing materials,but exhibits poor tribological performance,especially under the conditions of dry sliding friction.A Hydrogenated Diamond-Like Carbon(H-DLC)coating was deposited on the 60NiTi alloy to improve its tribological performance.The microstructure and mechanical behavior of the 60NiTi alloy and its H-DLC coating were explored.Results show that improvement of friction and wear performance of the H-DLC coating deposited on the 60NiTi substrate is mainly achieved by graphitization at the friction interface and the transfer film produced on the counterpart ball.The increased friction load leads to intensification of graphitization at the friction interface and formation of continuous and compact transfer film on the surface of the counterpart ball.
基金financially supported by the financial support from the International Postdoctoral Exchange Fellowship Program 2019 by the Office of China Postdoctoral Council (No. 20190086)the support from the Russian Science Foundation Grant (No. 19-79-30002)。
文摘Electrochemical tests and surface analysis were applied to study the corrosion behavior and passive film characteristics of three-dimensional-printed NiTi shape memory alloys fabricated by laser-powder bed fusion(LPBF) in artificial saliva at 37.C. The passivity of L-PBF NiTi shows to be influenced by the process parameters and resulting morphological and physicochemical surface properties. The results show that the defects at the surface of L-PBF Ni Ti can promote the passivation rate in the early stages of exposure but a slowly formed passive film shows the best corrosion protection. The thickness of the passive film is positively correlated with its corrosion protective performance. The L-PBF NiTi alloy prepared at a linear energy density of 0.2 J·m^(-1) and volumetric energy density of 56 J·mm^(-3) shows the least defects and best corrosion protection. An outer Ti-rich and inner Ni-rich dense passive film could be also obtained showing higher corrosion resistance.
基金The present work was financially supported by the Fundamental Research Funds for the Central Universities(xzy022019015)the National Natural Science Foundation of China(51675409).
文摘The microstructure,mechanical and micro/nano-tribological properties of the 60NiTi film annealed at different temperature were investigated.The results reveal that annealing as-deposited 60NiTi film at 300,375,and 600℃ for 1 h leads to structural relaxation,partial crystallization and full crystallization,respectively.Compared with the structurally relaxed structure,the partially crystallized structure exhibits increased hardness but decreased elastic modulus.This is because that the elastic modulus is reduced by Voigt model while the hardness is improved by composite effect.Due to the highest hardness and ratio of hardness to elastic modulus(H/E),the partially crystallized 60NiTi film has the lowest penetration depth and residual depth(i.e.,groove depth).Besides,the results also reveal that ductile plowing is the dominant wear mechanism for all the annealed 60NiTi films.Under the condition of the ductile plowing,coefficient of friction and wear resistance are related to penetration depth and residual depth,respectively.Therefore,the partially crystallized 60NiTi film shows the best tribological performance at the micro/nano-scale.The current work not only highlights the important roles of hardness and H/E in improving the micro/nano-tribological properties but also concludes an efficient and simple method for simultaneously increasing hardness and H/E.