Cu/ZrO2 catalysts for methanol synthesis from CO2/H2 were respectively prepared by deposition coprecipitation （DP） and solid state reaction （SR） methods. There is an intimate interaction between copper and zirconi...Cu/ZrO2 catalysts for methanol synthesis from CO2/H2 were respectively prepared by deposition coprecipitation （DP） and solid state reaction （SR） methods. There is an intimate interaction between copper and zirconia, which strongly affects the reduction property and catalytic performance of the catalysts. The stronger the interaction, the lower the reduction temperature and the better the performance of the catalysts. Surface area, pore structure and crystal structure of the catalysts are mainly controlled by preparation methods and alkalinity of synthesis system. The conversion of CO2 and selectivity of methanol are higher for DP catalysts than for SP catalysts.展开更多
A series of hybrid catalysts were made by physically mixing Cu-ZrO2 and γ-A12O3, for former it was modified with different loadings of La2O3 prepared by co-precipitation method. The catalysts were characterized by BE...A series of hybrid catalysts were made by physically mixing Cu-ZrO2 and γ-A12O3, for former it was modified with different loadings of La2O3 prepared by co-precipitation method. The catalysts were characterized by BET, XRD, N2O-adsorption, EXAFS, H2-TPR, NH3-TPD techniques and evaluated in the synthesis of dimethyl ether from syngas. The results show that La2O3 promoted catalysts displayed a significantly better catalytic performance compared with Cu-ZrO2#y-A12O3 catalyst in CO conversion and DME selectivity, and the optimum catalytic activity was obtained when the content of La2O3 was 12 wt%. The characterizations reveal that high copper dispersion, facile reducibility of copper particles and appropriate amount of acidic sites are responsible for the superior catalytic performance.展开更多
Cu/ZrO 2 and MoS 2 based catalysts were developed for the synthesis of higher alcohols. Modified by the carbon chain growth enhancing elements, both catalyst systems showed the high performance without the obvious dea...Cu/ZrO 2 and MoS 2 based catalysts were developed for the synthesis of higher alcohols. Modified by the carbon chain growth enhancing elements, both catalyst systems showed the high performance without the obvious deactivation after 2000 h running at 9.0～12.0 MPa and 300～380 ℃, indicating a good prospect for the further development in practical application.展开更多
文摘Cu/ZrO2 catalysts for methanol synthesis from CO2/H2 were respectively prepared by deposition coprecipitation （DP） and solid state reaction （SR） methods. There is an intimate interaction between copper and zirconia, which strongly affects the reduction property and catalytic performance of the catalysts. The stronger the interaction, the lower the reduction temperature and the better the performance of the catalysts. Surface area, pore structure and crystal structure of the catalysts are mainly controlled by preparation methods and alkalinity of synthesis system. The conversion of CO2 and selectivity of methanol are higher for DP catalysts than for SP catalysts.
基金supported by the Ministry of Science and Technology of the People’s Republic of China (No. 2011BAD22B06)the Chinese Academy of Sciences (No. GJHZ1025,Y2010022,KGCX2-YW-329)
文摘A series of hybrid catalysts were made by physically mixing Cu-ZrO2 and γ-A12O3, for former it was modified with different loadings of La2O3 prepared by co-precipitation method. The catalysts were characterized by BET, XRD, N2O-adsorption, EXAFS, H2-TPR, NH3-TPD techniques and evaluated in the synthesis of dimethyl ether from syngas. The results show that La2O3 promoted catalysts displayed a significantly better catalytic performance compared with Cu-ZrO2#y-A12O3 catalyst in CO conversion and DME selectivity, and the optimum catalytic activity was obtained when the content of La2O3 was 12 wt%. The characterizations reveal that high copper dispersion, facile reducibility of copper particles and appropriate amount of acidic sites are responsible for the superior catalytic performance.
文摘Cu/ZrO 2 and MoS 2 based catalysts were developed for the synthesis of higher alcohols. Modified by the carbon chain growth enhancing elements, both catalyst systems showed the high performance without the obvious deactivation after 2000 h running at 9.0～12.0 MPa and 300～380 ℃, indicating a good prospect for the further development in practical application.