A simple and rapid approach for the electrochemical synthesis of Ag nanoparticles-coated gold nanoporous film (AgGNF) on a gold substrate was reported. The solid gold electrode (SGE) was directly anodized under a high...A simple and rapid approach for the electrochemical synthesis of Ag nanoparticles-coated gold nanoporous film (AgGNF) on a gold substrate was reported. The solid gold electrode (SGE) was directly anodized under a high potential of 5 V, and then reduced to obtain gold nanoporous film (AuNF) by freshly prepared ascorbic acid. The Ag nanoparticles (AgNPs) were grown on the AuNF electrode by potential-step electrodeposition. The resulting AgGNF composites electrodes were characterized by scanning electron microscopy (SEM), energy dispersive X-ray (EDX) spectroscopy and cyclic voltammetry (CV). As-prepared AgGNF electrode was used as a kind of superior sensor for Cr(VI) detection, which exhibited better electrocatalytic behavior than those of AuNF and SGE under identical conditions. Such a designed AgGNF nanocomposites electrode showed outstanding sensitivity (about 0.15 nA/ppb) and favorable reproducibility for Cr(VI) detection. The dependence of reduction current on Cr(VI) concentration is linear from 2 to 370 ppb with a low detection limit of 0.65 ppb. Interferences from other heavy metals ions (Cr3+, Cu2+, Pb2+, As3+ and Hg2+) associated with Cr(VI) analysis could be effectively diminished. The present method proves to be rapid, reliable, sensitive and low-cost.展开更多
The coupling of upconversion nanophosphors （UCNPs） with the surface plasmonic resonance （SPR） of noble metals is a promising way to improve luminescent efficiency of UCNPs; however, it is still a challenge to achi...The coupling of upconversion nanophosphors （UCNPs） with the surface plasmonic resonance （SPR） of noble metals is a promising way to improve luminescent efficiency of UCNPs; however, it is still a challenge to achieve stable, reproducible and effective upconversion luminescence （UCL） enhancement through such coupling. In this work, we present a novel strategy to improve UCL of NaYF4：ybB,Er3. UCNPs, by combining the near-field coupling of SPR of silver and the far-field coupling of poly（methyl methacrylate） （PMMA） opal photonic crystals （OPCs） with the UCNPs. In order to control the effective interaction distance between the UCNPs and the SPR, a porous silver film consisting of randomly distributed silver nanoparticles （NPs） （〉 100 nm） was prepared which demonstrated strong SPR over a broad wavelength range, and its coupling to the UCNPs was found to be much stronger than that of a dense film. In the far-field coupling of OPCs, the photonic stop band （PSB） of the PMMA OPCs was tuned to 980 nm, matching exactly the excitation light. By modulating the particle size of the UCNPs, and the direction and excitation power of the incident light, a maximum enhancement of 60-fold was observed, which is an important advance for metaMnduced UCL enhancement systems.展开更多
Due to its lead-free composition and a unique double polarization hysteresis loop with a large maximum polarization(Pmax)and a small remnant polarization(Pr),AgNbO_(3)-based antiferroelectrics(AFEs)have attracted exte...Due to its lead-free composition and a unique double polarization hysteresis loop with a large maximum polarization(Pmax)and a small remnant polarization(Pr),AgNbO_(3)-based antiferroelectrics(AFEs)have attracted extensive research interest for electric energy storage applications.However,a low dielectric breakdown field(Eb)limits an energy density and its further development.In this work,a highly efficient method was proposed to fabricate high-energy-density Ag(Nb,Ta)O_(3) capacitor films on Si substrates,using a two-step process combining radio frequency(RF)-magnetron sputtering at 450℃and post-deposition rapid thermal annealing(RTA).The RTA process at 700℃led to sufficient crystallization of nanograins in the film,hindering their lateral growth by employing short annealing time of 5 min.The obtained Ag(Nb,Ta)O_(3) films showed an average grain size(D)of~14 nm(obtained by Debye-Scherrer formula)and a slender room temperature(RT)polarization-electric field(P-E)loop(Pr≈3.8 mC·cm^(−2) and P_(max)≈38 mC·cm^(−2) under an electric field of~3.3 MV·cm^(−1)),the P-E loop corresponding to a high recoverable energy density(W_(rec))of~46.4 J·cm^(−3) and an energy efficiency(η)of~80.3%.Additionally,by analyzing temperature-dependent dielectric property of the film,a significant downshift of the diffused phase transition temperature(T_(M2-M3))was revealed,which indicated the existence of a stable relaxor-like AFE phase near the RT.The downshift of the T_(M2-M3) could be attributed to a nanograin size and residual tensile strain of the film,and it led to excellent temperature stability(20-240℃)of the energy storage performance of the film.Our results indicate that the Ag(Nb,Ta)O_(3) film is a promising candidate for electrical energy storage applications.展开更多
The process of preparing anodic oxide film containing active sites and electroless nickel plating on highly active rare earth magnesium alloy was developed.The formation mechanism of electroless nickel plating on acti...The process of preparing anodic oxide film containing active sites and electroless nickel plating on highly active rare earth magnesium alloy was developed.The formation mechanism of electroless nickel plating on active anodic oxide film and the structure and properties of the composite coating were studied by several surface and electrochemical techniques.The results showed that Ag nanograins with an average size of 10 nm were embedded into the anodic oxide film with pores of 0.1−2μm.Ag nanoparticles provided a catalytic site for the deposition of Ni-B alloy,and the Ni crystal nucleus was first grown in horizontal mode and then in cylindrical mode.The corrosion potential of the composite coating increased by 1.37 V and the corrosion current reduced two orders of magnitude due to the subsequent deposition of Ni-P alloy.The high corrosion resistance was attributed to the misaligning of these micro defects in the three different layers and the amorphous structure of the Ni-P alloy in the outer layer.These findings provide a new idea for electroless nickel plating on anodic oxide film.展开更多
基金supported by the National Natural Science Foundation of China (21005014)the Foundation of Donghua University (113-10-0044029)
文摘A simple and rapid approach for the electrochemical synthesis of Ag nanoparticles-coated gold nanoporous film (AgGNF) on a gold substrate was reported. The solid gold electrode (SGE) was directly anodized under a high potential of 5 V, and then reduced to obtain gold nanoporous film (AuNF) by freshly prepared ascorbic acid. The Ag nanoparticles (AgNPs) were grown on the AuNF electrode by potential-step electrodeposition. The resulting AgGNF composites electrodes were characterized by scanning electron microscopy (SEM), energy dispersive X-ray (EDX) spectroscopy and cyclic voltammetry (CV). As-prepared AgGNF electrode was used as a kind of superior sensor for Cr(VI) detection, which exhibited better electrocatalytic behavior than those of AuNF and SGE under identical conditions. Such a designed AgGNF nanocomposites electrode showed outstanding sensitivity (about 0.15 nA/ppb) and favorable reproducibility for Cr(VI) detection. The dependence of reduction current on Cr(VI) concentration is linear from 2 to 370 ppb with a low detection limit of 0.65 ppb. Interferences from other heavy metals ions (Cr3+, Cu2+, Pb2+, As3+ and Hg2+) associated with Cr(VI) analysis could be effectively diminished. The present method proves to be rapid, reliable, sensitive and low-cost.
文摘The coupling of upconversion nanophosphors （UCNPs） with the surface plasmonic resonance （SPR） of noble metals is a promising way to improve luminescent efficiency of UCNPs; however, it is still a challenge to achieve stable, reproducible and effective upconversion luminescence （UCL） enhancement through such coupling. In this work, we present a novel strategy to improve UCL of NaYF4：ybB,Er3. UCNPs, by combining the near-field coupling of SPR of silver and the far-field coupling of poly（methyl methacrylate） （PMMA） opal photonic crystals （OPCs） with the UCNPs. In order to control the effective interaction distance between the UCNPs and the SPR, a porous silver film consisting of randomly distributed silver nanoparticles （NPs） （〉 100 nm） was prepared which demonstrated strong SPR over a broad wavelength range, and its coupling to the UCNPs was found to be much stronger than that of a dense film. In the far-field coupling of OPCs, the photonic stop band （PSB） of the PMMA OPCs was tuned to 980 nm, matching exactly the excitation light. By modulating the particle size of the UCNPs, and the direction and excitation power of the incident light, a maximum enhancement of 60-fold was observed, which is an important advance for metaMnduced UCL enhancement systems.
基金support from the National Natural Science Foundation of China (Grant Nos.51772175,52072218,and 52002192)Natural Science Foundation of Shandong Province (Grant Nos.ZR2020QE042,ZR2022ZD39,and ZR2022ME031)+6 种基金the Science,Education and Industry Integration Pilot Projects of Qilu University of Technology (Shandong Academy of Sciences) (Grant Nos.2022GH018 and 2022PY055)support from the Jinan City Science and Technology Bureau (Grant No.2021GXRC055)the Education Department of Hunan Province/Xiangtan University (Grant No.KZ0807969)funding for top talents at Qilu University of Technology (Shandong Academy of Sciences)support from the Jiangsu Province NSFC (Grant No.BK20180764)support from the National Key R&D Program of China (Grant No.2021YFB3601504)Natural Science Foundation of Shandong Province (Grant No.ZR2020KE019).
文摘Due to its lead-free composition and a unique double polarization hysteresis loop with a large maximum polarization(Pmax)and a small remnant polarization(Pr),AgNbO_(3)-based antiferroelectrics(AFEs)have attracted extensive research interest for electric energy storage applications.However,a low dielectric breakdown field(Eb)limits an energy density and its further development.In this work,a highly efficient method was proposed to fabricate high-energy-density Ag(Nb,Ta)O_(3) capacitor films on Si substrates,using a two-step process combining radio frequency(RF)-magnetron sputtering at 450℃and post-deposition rapid thermal annealing(RTA).The RTA process at 700℃led to sufficient crystallization of nanograins in the film,hindering their lateral growth by employing short annealing time of 5 min.The obtained Ag(Nb,Ta)O_(3) films showed an average grain size(D)of~14 nm(obtained by Debye-Scherrer formula)and a slender room temperature(RT)polarization-electric field(P-E)loop(Pr≈3.8 mC·cm^(−2) and P_(max)≈38 mC·cm^(−2) under an electric field of~3.3 MV·cm^(−1)),the P-E loop corresponding to a high recoverable energy density(W_(rec))of~46.4 J·cm^(−3) and an energy efficiency(η)of~80.3%.Additionally,by analyzing temperature-dependent dielectric property of the film,a significant downshift of the diffused phase transition temperature(T_(M2-M3))was revealed,which indicated the existence of a stable relaxor-like AFE phase near the RT.The downshift of the T_(M2-M3) could be attributed to a nanograin size and residual tensile strain of the film,and it led to excellent temperature stability(20-240℃)of the energy storage performance of the film.Our results indicate that the Ag(Nb,Ta)O_(3) film is a promising candidate for electrical energy storage applications.
基金Project(5227010679)supported by the National Natural Science Foundation of China。
文摘The process of preparing anodic oxide film containing active sites and electroless nickel plating on highly active rare earth magnesium alloy was developed.The formation mechanism of electroless nickel plating on active anodic oxide film and the structure and properties of the composite coating were studied by several surface and electrochemical techniques.The results showed that Ag nanograins with an average size of 10 nm were embedded into the anodic oxide film with pores of 0.1−2μm.Ag nanoparticles provided a catalytic site for the deposition of Ni-B alloy,and the Ni crystal nucleus was first grown in horizontal mode and then in cylindrical mode.The corrosion potential of the composite coating increased by 1.37 V and the corrosion current reduced two orders of magnitude due to the subsequent deposition of Ni-P alloy.The high corrosion resistance was attributed to the misaligning of these micro defects in the three different layers and the amorphous structure of the Ni-P alloy in the outer layer.These findings provide a new idea for electroless nickel plating on anodic oxide film.