Microstructure and tensile properties of TC21 titanium alloy after near-isothermal forging with different parameters plus solution treatment and aging were investigated. It is found that the residual β matrix, which ...Microstructure and tensile properties of TC21 titanium alloy after near-isothermal forging with different parameters plus solution treatment and aging were investigated. It is found that the residual β matrix, which was strengthened by fine secondary α platelets forming during aging, exists in all the samples; while primary equiaxed α phase, bent lamellar α phase and α plates are simultaneously or individually present in one sample. The strength of alloy increases proportionally with increasing the content of residual β matrix, which is the result of increasing α/β interphase boundary. The plasticity of alloy has a downward trend as the content of residual β matrix increases. This attributes to the increase of fine secondary α platelets, which are cut by dislocations during the deformation. Additionally, coarse α plates with long axis parallel to the maximum resolved shear stress（MRSS） also reduce the plasticity of TC21 alloy.展开更多
The 12 mm-thick Ti−6Al−4V(TC4)titanium alloy plates were welded using keyhole tungsten inert gas(K-TIG)welding at various heat inputs.The microstructure,grain boundary(GB)characteristics and mechanical properties of t...The 12 mm-thick Ti−6Al−4V(TC4)titanium alloy plates were welded using keyhole tungsten inert gas(K-TIG)welding at various heat inputs.The microstructure,grain boundary(GB)characteristics and mechanical properties of the weld metal zone(WMZ)were analyzed.The test results show that the K-TIG welds are well formed,and no obvious defects are observed when the heat input is 2.30−2.62 kJ/mm.When the heat input gradually increases,αlaths increase in length,andα′phase and residualβphase are reduced.The electron backscatter diffraction(EBSD)test results indicate that the high-angle GB proportion in the WMZ increases with the increase of heat input.The tensile strength of the WMZ gradually decreases and the elongation of the WMZ increases when the heat input increases from 2.30 to 2.62 kJ/mm.The impact toughness of the WMZ increases as the heat input increases.展开更多
Taking a Ti−5Al−5Mo−5V−1Cr−1Fe alloy as exemplary case,the fatigue crack growth sensitivity and fracture features with various tailoredαphase morphologies were thoroughly investigated using fatigue crack growth rate(...Taking a Ti−5Al−5Mo−5V−1Cr−1Fe alloy as exemplary case,the fatigue crack growth sensitivity and fracture features with various tailoredαphase morphologies were thoroughly investigated using fatigue crack growth rate(FCGR)test,optical microscopy(OM)and scanning electron microscopy(SEM).The tailored microstructures by heat treatments include the fine and coarse secondaryαphase,as well as the widmanstatten and basket weave features.The sample with coarse secondaryαphase exhibits better comprehensive properties of good crack propagation resistance(with long Paris regime ranging from 15 to 60 MPa·m1/2),high yield strength(1113 MPa)and ultimate strength(1150 MPa),and good elongation(11.6%).The good crack propagation resistance can be attributed to crack deflection,long secondary crack,and tortuous crack path induced by coarse secondaryαphase.展开更多
基金Projects(51205319,51101119)supported by the National Natural Science Foundation of China
文摘Microstructure and tensile properties of TC21 titanium alloy after near-isothermal forging with different parameters plus solution treatment and aging were investigated. It is found that the residual β matrix, which was strengthened by fine secondary α platelets forming during aging, exists in all the samples; while primary equiaxed α phase, bent lamellar α phase and α plates are simultaneously or individually present in one sample. The strength of alloy increases proportionally with increasing the content of residual β matrix, which is the result of increasing α/β interphase boundary. The plasticity of alloy has a downward trend as the content of residual β matrix increases. This attributes to the increase of fine secondary α platelets, which are cut by dislocations during the deformation. Additionally, coarse α plates with long axis parallel to the maximum resolved shear stress（MRSS） also reduce the plasticity of TC21 alloy.
基金The authors are grateful for the financial supports from the Key Research and Development Program of Guangdong Province,China(2020B090928003)the Natural Science Foundation of Guangdong Province,China(2020A1515011050)+1 种基金the Science and Technology Base and Talent Special Project of Guangxi Province,China(AD19245150)Guangxi University of Science and Technology Doctoral Fund,China(19Z27).
文摘The 12 mm-thick Ti−6Al−4V(TC4)titanium alloy plates were welded using keyhole tungsten inert gas(K-TIG)welding at various heat inputs.The microstructure,grain boundary(GB)characteristics and mechanical properties of the weld metal zone(WMZ)were analyzed.The test results show that the K-TIG welds are well formed,and no obvious defects are observed when the heat input is 2.30−2.62 kJ/mm.When the heat input gradually increases,αlaths increase in length,andα′phase and residualβphase are reduced.The electron backscatter diffraction(EBSD)test results indicate that the high-angle GB proportion in the WMZ increases with the increase of heat input.The tensile strength of the WMZ gradually decreases and the elongation of the WMZ increases when the heat input increases from 2.30 to 2.62 kJ/mm.The impact toughness of the WMZ increases as the heat input increases.
基金Project(U1867201)supported by the National Natural Science Foundation of ChinaProject supported by State Key Laboratory of Powder Metallurgy,Central South University,China。
文摘Taking a Ti−5Al−5Mo−5V−1Cr−1Fe alloy as exemplary case,the fatigue crack growth sensitivity and fracture features with various tailoredαphase morphologies were thoroughly investigated using fatigue crack growth rate(FCGR)test,optical microscopy(OM)and scanning electron microscopy(SEM).The tailored microstructures by heat treatments include the fine and coarse secondaryαphase,as well as the widmanstatten and basket weave features.The sample with coarse secondaryαphase exhibits better comprehensive properties of good crack propagation resistance(with long Paris regime ranging from 15 to 60 MPa·m1/2),high yield strength(1113 MPa)and ultimate strength(1150 MPa),and good elongation(11.6%).The good crack propagation resistance can be attributed to crack deflection,long secondary crack,and tortuous crack path induced by coarse secondaryαphase.