To meet the processing requirements of resin transfer moulding(RTM)technology,reactive diluent containing m-phenylene moiety was synthesized to physically mixed with phenylethynyl terminated cooligoimides with well-de...To meet the processing requirements of resin transfer moulding(RTM)technology,reactive diluent containing m-phenylene moiety was synthesized to physically mixed with phenylethynyl terminated cooligoimides with well-designed molecular weights of 1500-2500 g/mol derived from 4,4’-(hexafluoroisopropylidene)diphthalic anhydride(6 FDA),3,4’-oxydianiline(3,4’-ODA)and m-phenylenediamine(m-PDA).This blend shows low minimum melting viscosity(<1 Pa·s)and enlarged processing temperature window(260–361℃).FPI-R-1 stays below 1 Pa·s for2 h at 270℃.The relationship between the molecular weight of the blend and its melting stability was first explored.Blending oligoimides with lower molecular weights exhibit better melting stability.Upon curing at 380℃for 2 h,the thermosetting polyimide resin demonstrates superior heat resistance(T_(g)=420-426℃).展开更多
This study focuses on the thermo-mechanical properties of Carbon Fibre/Polyimide Composite(CFPC)attaching collars under transient heating.The CFPC attaching collars were fabricated by a high-temperature resin transfer...This study focuses on the thermo-mechanical properties of Carbon Fibre/Polyimide Composite(CFPC)attaching collars under transient heating.The CFPC attaching collars were fabricated by a high-temperature resin transfer moulding process,and their thermo-mechanical properties under the conditions of simultaneous transient heating and bending load were investigated.The results show that the attaching collar tends to fail at 118% of the limit load.The failure mode includes the fracture of the connecting screws,local extrusion damage of the hole edges,and slight ablation damage at the outer plies.And there is no observable residual deformation in the composite attaching collar.Furthermore,considering that the material properties vary with temperature,a progressive damage model based on the sequential thermo-mechanical coupling method was established to study the failure mechanism of the attaching collar.Finally,the damage factor of the CFPC was calculated to assess the safety status of the attaching collar.The results show that the primary damage modes of the composite attaching collar are intralaminar failure,which mainly occurs at the heat insulation layer and the hole edges,and these slightly affect the structural bearing capacity.A good correlation between the experiment and FEA is obtained.The test methods and analysis models proposed contribute to the safety assessment of composite structures under transient heating.展开更多
The successful manufacture of thick composites is challenging since the highly exothermic nature of thermoset resins and limited temperature control make avoiding the onset of detrimental thermal gradients within the ...The successful manufacture of thick composites is challenging since the highly exothermic nature of thermoset resins and limited temperature control make avoiding the onset of detrimental thermal gradients within the composite relatively difficult.This phenomenon is mainly caused by exothermic heat reactions.The so-called Michaud's model has been largely used in the literature to reduce the gap between experience and simulation with regard to the effective prediction of the temperature cycle in these processes.In this work,another solution is proposed to simulate the curing process for thick composites,namely preheating the resin to activate the curing reaction before resin injection into the mold.A good agreement between the experiment and the simulation is found.Moreover,in order to minimize the thermal gradient in the final composite,the thermophysical properties of the fiber and the torque(temperature,time)of the Plate have been varied leading to interesting results.展开更多
Deep petroleum resources are in a high-temperature environment.However,the traditional deep rock coring method has no temperature preserved measures and ignores the effect of temperature on rock porosity and permeabil...Deep petroleum resources are in a high-temperature environment.However,the traditional deep rock coring method has no temperature preserved measures and ignores the effect of temperature on rock porosity and permeability,which will lead to the distortion of the petroleum resources reserves assessment.Therefore,the hollow glass microspheres/epoxy resin(HGM/EP)composites were innovatively proposed as temperature preserved materials for in-situ temperature-preserved coring(ITP-Coring),and the physical,mechanical,and temperature preserved properties were evaluated.The results indicated that:As the HGM content increased,the density and mechanical properties of the composites gradually decreased,while the water absorption was deficient without hydrostatic pressure.For composites with 50 vol%HGM,when the hydrostatic pressure reached 60 MPa,the water absorption was above 30.19%,and the physical and mechanical properties of composites were weakened.When the hydrostatic pressure was lower than 40 MPa,the mechanical properties and thermal conductivity of composites were almost unchanged.Therefore,the composites with 50 vol%HGM can be used for ITPCoring operations in deep environments with the highest hydrostatic pressure of 40 MPa.Finally,to further understand the temperature preserved performance of composites in practical applications,the temperature preserved properties were measured.An unsteady-state heat transfer model was established based on the test results,then the theoretical change of the core temperature during the coring process was obtained.The above tests results can provide a research basis for deep rock in-situ temperature preserved corer and support accurate assessment of deep petroleum reserves.展开更多
This paper measured permeability of three-dimension braided preform by radial technology. The results show that principal permeability tensor coincided with their braiding axial direction. The software of one dimensio...This paper measured permeability of three-dimension braided preform by radial technology. The results show that principal permeability tensor coincided with their braiding axial direction. The software of one dimensional flow filling mold was designed using Visual C++ language. Filling time is predicted and validated. The result showed that the filling time of the mold centerline agrees with the prediction value. The filling time of the mould edge is shorter than that of the prediction. An actual plate of 3D braided preform/ modified polyarylacetylene composite is produced according to prediction value and validation analysis.展开更多
The equilibrium and kinetic characteristics of the adsorption of erythromycin to Sepabeads SP825 were determined.The equilibrium data in a batch system was well described by a Langmuir isotherm.The separation performa...The equilibrium and kinetic characteristics of the adsorption of erythromycin to Sepabeads SP825 were determined.The equilibrium data in a batch system was well described by a Langmuir isotherm.The separation performance was investigated in a fixed-bed system with respect to the adsorption superficial velocity,ionic strength and pH.A mathematical model was used to simulate the mass transfer mechanism,taking film mass transfer,pore diffusion and axial dispersion into account.The model predictions were consistent with the experi-mental data and were consequently used to determine the mass transfer coefficients.展开更多
A three-dimensional finite element analysis of process-induced residual stress in resin transfer molding (RTM) process is presented. The finite element method (FEM) was employed to solve the coupled equations involved...A three-dimensional finite element analysis of process-induced residual stress in resin transfer molding (RTM) process is presented. The finite element method (FEM) was employed to solve the coupled equations involved in the transient heat transfer and the cure kinetics of the resin, and the distributions of internal temperature and cure degree of the composite at any instant time were obtained. The self-consistent field micro-mechanics model was used to predict the cure-dependent mechanical properties of the composites. Thermal expansion and cure shrinkage were included in the analysis. The thermo-elastic mechanical governing equations were solved using the incremental stress-strain relationship based FEM and the residual stress development was predicted. The present results were validated by the comparisons with the pertinent literature. The numerical example of a half cylinder was presented. The results show that it is necessary to carry out the three-dimensional analysis due to the complex distributions of temperatures, cure degrees and process-induced stress for thick parts, which can be predicted at any point within composite structures in the present analysis.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51803222)Science and Technology Service Network Initiative,Chinese Academy of Sciences。
文摘To meet the processing requirements of resin transfer moulding(RTM)technology,reactive diluent containing m-phenylene moiety was synthesized to physically mixed with phenylethynyl terminated cooligoimides with well-designed molecular weights of 1500-2500 g/mol derived from 4,4’-(hexafluoroisopropylidene)diphthalic anhydride(6 FDA),3,4’-oxydianiline(3,4’-ODA)and m-phenylenediamine(m-PDA).This blend shows low minimum melting viscosity(<1 Pa·s)and enlarged processing temperature window(260–361℃).FPI-R-1 stays below 1 Pa·s for2 h at 270℃.The relationship between the molecular weight of the blend and its melting stability was first explored.Blending oligoimides with lower molecular weights exhibit better melting stability.Upon curing at 380℃for 2 h,the thermosetting polyimide resin demonstrates superior heat resistance(T_(g)=420-426℃).
基金supported by the Young Elite Scientists Sponsorship Program by the China Association for Science and Technology(No.2016QNRC001)the Science and Technology Commission of Shanghai Municipality,China(No.19DZ1100300)。
文摘This study focuses on the thermo-mechanical properties of Carbon Fibre/Polyimide Composite(CFPC)attaching collars under transient heating.The CFPC attaching collars were fabricated by a high-temperature resin transfer moulding process,and their thermo-mechanical properties under the conditions of simultaneous transient heating and bending load were investigated.The results show that the attaching collar tends to fail at 118% of the limit load.The failure mode includes the fracture of the connecting screws,local extrusion damage of the hole edges,and slight ablation damage at the outer plies.And there is no observable residual deformation in the composite attaching collar.Furthermore,considering that the material properties vary with temperature,a progressive damage model based on the sequential thermo-mechanical coupling method was established to study the failure mechanism of the attaching collar.Finally,the damage factor of the CFPC was calculated to assess the safety status of the attaching collar.The results show that the primary damage modes of the composite attaching collar are intralaminar failure,which mainly occurs at the heat insulation layer and the hole edges,and these slightly affect the structural bearing capacity.A good correlation between the experiment and FEA is obtained.The test methods and analysis models proposed contribute to the safety assessment of composite structures under transient heating.
文摘The successful manufacture of thick composites is challenging since the highly exothermic nature of thermoset resins and limited temperature control make avoiding the onset of detrimental thermal gradients within the composite relatively difficult.This phenomenon is mainly caused by exothermic heat reactions.The so-called Michaud's model has been largely used in the literature to reduce the gap between experience and simulation with regard to the effective prediction of the temperature cycle in these processes.In this work,another solution is proposed to simulate the curing process for thick composites,namely preheating the resin to activate the curing reaction before resin injection into the mold.A good agreement between the experiment and the simulation is found.Moreover,in order to minimize the thermal gradient in the final composite,the thermophysical properties of the fiber and the torque(temperature,time)of the Plate have been varied leading to interesting results.
基金National Natural Science Foundation of China(grant number 51827901)funded by the Program for Guangdong Introducing Innovative and Enterpreneurial Teams(No.2019ZT08G315)Shenzhen Basic Research Program(General Program)(No.JCYJ20190808153416970)
文摘Deep petroleum resources are in a high-temperature environment.However,the traditional deep rock coring method has no temperature preserved measures and ignores the effect of temperature on rock porosity and permeability,which will lead to the distortion of the petroleum resources reserves assessment.Therefore,the hollow glass microspheres/epoxy resin(HGM/EP)composites were innovatively proposed as temperature preserved materials for in-situ temperature-preserved coring(ITP-Coring),and the physical,mechanical,and temperature preserved properties were evaluated.The results indicated that:As the HGM content increased,the density and mechanical properties of the composites gradually decreased,while the water absorption was deficient without hydrostatic pressure.For composites with 50 vol%HGM,when the hydrostatic pressure reached 60 MPa,the water absorption was above 30.19%,and the physical and mechanical properties of composites were weakened.When the hydrostatic pressure was lower than 40 MPa,the mechanical properties and thermal conductivity of composites were almost unchanged.Therefore,the composites with 50 vol%HGM can be used for ITPCoring operations in deep environments with the highest hydrostatic pressure of 40 MPa.Finally,to further understand the temperature preserved performance of composites in practical applications,the temperature preserved properties were measured.An unsteady-state heat transfer model was established based on the test results,then the theoretical change of the core temperature during the coring process was obtained.The above tests results can provide a research basis for deep rock in-situ temperature preserved corer and support accurate assessment of deep petroleum reserves.
文摘This paper measured permeability of three-dimension braided preform by radial technology. The results show that principal permeability tensor coincided with their braiding axial direction. The software of one dimensional flow filling mold was designed using Visual C++ language. Filling time is predicted and validated. The result showed that the filling time of the mold centerline agrees with the prediction value. The filling time of the mould edge is shorter than that of the prediction. An actual plate of 3D braided preform/ modified polyarylacetylene composite is produced according to prediction value and validation analysis.
文摘The equilibrium and kinetic characteristics of the adsorption of erythromycin to Sepabeads SP825 were determined.The equilibrium data in a batch system was well described by a Langmuir isotherm.The separation performance was investigated in a fixed-bed system with respect to the adsorption superficial velocity,ionic strength and pH.A mathematical model was used to simulate the mass transfer mechanism,taking film mass transfer,pore diffusion and axial dispersion into account.The model predictions were consistent with the experi-mental data and were consequently used to determine the mass transfer coefficients.
基金the National Natural Science Foundation of China(Grant No.10502016)Development Program for Outstanding Young Teachers in Harbin Institute of Technology(Grant No.HITQNJS.2006.020)
文摘A three-dimensional finite element analysis of process-induced residual stress in resin transfer molding (RTM) process is presented. The finite element method (FEM) was employed to solve the coupled equations involved in the transient heat transfer and the cure kinetics of the resin, and the distributions of internal temperature and cure degree of the composite at any instant time were obtained. The self-consistent field micro-mechanics model was used to predict the cure-dependent mechanical properties of the composites. Thermal expansion and cure shrinkage were included in the analysis. The thermo-elastic mechanical governing equations were solved using the incremental stress-strain relationship based FEM and the residual stress development was predicted. The present results were validated by the comparisons with the pertinent literature. The numerical example of a half cylinder was presented. The results show that it is necessary to carry out the three-dimensional analysis due to the complex distributions of temperatures, cure degrees and process-induced stress for thick parts, which can be predicted at any point within composite structures in the present analysis.