The effects of Al substitution for Fe on the structure, magnetics, magnetostriction, anisotropy and spin reorientation of a series of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 alloys (x=0.05, 0.1, 0.15, 0.2, 0.25, 0.3) at room te...The effects of Al substitution for Fe on the structure, magnetics, magnetostriction, anisotropy and spin reorientation of a series of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 alloys (x=0.05, 0.1, 0.15, 0.2, 0.25, 0.3) at room temperature have been investigated. The alloys of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 substantially retain MgCu2-type C-15 cubic Laves phase structure when x【0.2. The mixed phases appear with x = 0.2, and cubic Laves phase decreases with increasing x. The magnetostriction of the Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 alloys decreases drastically with increasing x and the giant magnetostrictive effect disappears for x 】 0.15. Fortunately, a small amount of Al substitution is beneficial to a decrease in the magnetocrystalline anisotropy. The spin reorientation temperature decreases with increasing x. The analysis of the Mssbauer spectra indicates that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry with the increase of Al concentration x, namely, spin reorientation, resulting in the change of macroscopical magnetic properties and magnetostriction. The hyperfine field decreases, but the isomer shifts increases with Al concentration increasing and the quadruple splitting QS shows a weak concentration dependence.展开更多
The effect of the orientation on the magnetostriction in Fe81Ga19 alloy has been investigated experimentally and theoretically. The Fe81Ca19 [001] and [110] oriented crystals were prepared and the magnetostriction was...The effect of the orientation on the magnetostriction in Fe81Ga19 alloy has been investigated experimentally and theoretically. The Fe81Ca19 [001] and [110] oriented crystals were prepared and the magnetostriction was measured under different pre-stress. The saturation magnetostriction of the [001] oriented crystal increases from 170×10^-6 to 330×10^-6 under the pre-stress from 0 to 50 MPa. The [110] oriented crystal has a saturation magnetostriction from 20×10^-6 to 140×10^-6 with the compressive pre-stress from 0 to 40 MPa. The magnetostriction of [001] and [110] oriented crystals has been simulated based on the phenomenological theory. The domain rotation path has been determined and the resultant magnetostriction calculated under different pre-stress. The experimental and simulated results both show that the [001] oriented crystal exhibits better magnetostriction than [110] oriented crystal. The enhancement of the saturation magnetostriction by the compressive pre-stress in the [110] oriented crystal is higher than that in the [001] oriented crystal.展开更多
基金supported by the National Natural Science Foundation of China (Grant No. 10574059)the Natural Science Foundation of Gansu Province (Grant No. 0710RJZA074)+2 种基金the Scientific Research Project of Bureau of Education of Gansu Province (Grant No. 0711B-04)the Key Project of the Science and Technology Research of Ministry of Education (Grant No. 209127)the "Qing Lan" Talent Engineering Funds of Lanzhou Jiaotong University
文摘The effects of Al substitution for Fe on the structure, magnetics, magnetostriction, anisotropy and spin reorientation of a series of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 alloys (x=0.05, 0.1, 0.15, 0.2, 0.25, 0.3) at room temperature have been investigated. The alloys of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 substantially retain MgCu2-type C-15 cubic Laves phase structure when x【0.2. The mixed phases appear with x = 0.2, and cubic Laves phase decreases with increasing x. The magnetostriction of the Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 alloys decreases drastically with increasing x and the giant magnetostrictive effect disappears for x 】 0.15. Fortunately, a small amount of Al substitution is beneficial to a decrease in the magnetocrystalline anisotropy. The spin reorientation temperature decreases with increasing x. The analysis of the Mssbauer spectra indicates that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry with the increase of Al concentration x, namely, spin reorientation, resulting in the change of macroscopical magnetic properties and magnetostriction. The hyperfine field decreases, but the isomer shifts increases with Al concentration increasing and the quadruple splitting QS shows a weak concentration dependence.
基金Project supported by the Key Program of the National Natural Science Foundation of China (Grant No. 50531010)National Science Fund for Distinguished Young Scholars of China (Grant No. 50925101)Science Fund for Creative Research Groups of the National Natural Science Foundation of China (Grant No. 50921003)
文摘The effect of the orientation on the magnetostriction in Fe81Ga19 alloy has been investigated experimentally and theoretically. The Fe81Ca19 [001] and [110] oriented crystals were prepared and the magnetostriction was measured under different pre-stress. The saturation magnetostriction of the [001] oriented crystal increases from 170×10^-6 to 330×10^-6 under the pre-stress from 0 to 50 MPa. The [110] oriented crystal has a saturation magnetostriction from 20×10^-6 to 140×10^-6 with the compressive pre-stress from 0 to 40 MPa. The magnetostriction of [001] and [110] oriented crystals has been simulated based on the phenomenological theory. The domain rotation path has been determined and the resultant magnetostriction calculated under different pre-stress. The experimental and simulated results both show that the [001] oriented crystal exhibits better magnetostriction than [110] oriented crystal. The enhancement of the saturation magnetostriction by the compressive pre-stress in the [110] oriented crystal is higher than that in the [001] oriented crystal.