摘要
The effects of Al substitution for Fe on the structure, magnetics, magnetostriction, anisotropy and spin reorientation of a series of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 alloys (x=0.05, 0.1, 0.15, 0.2, 0.25, 0.3) at room temperature have been investigated. The alloys of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 substantially retain MgCu2-type C-15 cubic Laves phase structure when x【0.2. The mixed phases appear with x = 0.2, and cubic Laves phase decreases with increasing x. The magnetostriction of the Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 alloys decreases drastically with increasing x and the giant magnetostrictive effect disappears for x 】 0.15. Fortunately, a small amount of Al substitution is beneficial to a decrease in the magnetocrystalline anisotropy. The spin reorientation temperature decreases with increasing x. The analysis of the Mssbauer spectra indicates that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry with the increase of Al concentration x, namely, spin reorientation, resulting in the change of macroscopical magnetic properties and magnetostriction. The hyperfine field decreases, but the isomer shifts increases with Al concentration increasing and the quadruple splitting QS shows a weak concentration dependence.
The effects of Al substitution for Fe on the structure, magnetics, magnetostriction, anisotropy and spin reorientation of a series of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 alloys (x=0.05, 0.1, 0.15, 0.2, 0.25, 0.3) at room temperature have been investigated. The alloys of Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 substantially retain MgCu2-type C-15 cubic Laves phase structure when x<0.2. The mixed phases appear with x = 0.2, and cubic Laves phase decreases with increasing x. The magnetostriction of the Tb0.3Dy0.6Pr0.1(Fe1-xAlx)1.95 alloys decreases drastically with increasing x and the giant magnetostrictive effect disappears for x > 0.15. Fortunately, a small amount of Al substitution is beneficial to a decrease in the magnetocrystalline anisotropy. The spin reorientation temperature decreases with increasing x. The analysis of the Mssbauer spectra indicates that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry with the increase of Al concentration x, namely, spin reorientation, resulting in the change of macroscopical magnetic properties and magnetostriction. The hyperfine field decreases, but the isomer shifts increases with Al concentration increasing and the quadruple splitting QS shows a weak concentration dependence.
作者
ZHENG XiaoPing1,3, ZHANG PeiFeng1,2, LI FaShen2 & HAO Yuan2 1 Institute of Electronic Information Science and Technology, Lanzhou City University, Lanzhou 730070, China
2 Key Laboratory for Magnetism and Magnetic Materials, Ministry of Education, Lanzhou University, Lanzhou 730000, China
3 State Key Laboratory of Advanced Non-Ferrous Materials, Gansu Province, Lanzhou University of Technology, Lanzhou 730050, China
基金
supported by the National Natural Science Foundation of China (Grant No. 10574059)
the Natural Science Foundation of Gansu Province (Grant No. 0710RJZA074)
the Scientific Research Project of Bureau of Education of Gansu Province (Grant No. 0711B-04)
the Key Project of the Science and Technology Research of Ministry of Education (Grant No. 209127)
the "Qing Lan" Talent Engineering Funds of Lanzhou Jiaotong University