BNi-2/WC composite wear-resisting coating was prepared on carbon steel by the method of induction brazing.The microstructure and phase composition of the composite coating were analyzed,and the bonding strength and we...BNi-2/WC composite wear-resisting coating was prepared on carbon steel by the method of induction brazing.The microstructure and phase composition of the composite coating were analyzed,and the bonding strength and wear-resisting performance of the coating were tested.During the process of induction brazing,the tungsten carbide partially dissolves and reacts with the filler metal alloy to form NiW compound phase,which realizes the metallurgical combination of tungsten carbide and filler metal alloy.The matrix of the filler metal alloy consists of Ni solid solution and Ni_(3)B/Ni_(3)Si eutectic phase,and the metallurgical diffusion reaction occurs between the filler metal alloy and the steel matrix.The mechanical analysis results show that the self-strength of the composite coating reaches 140 MPa and the bonding strength of the filler metal alloy to the steel matrix reaches 360 MPa.The dry sand rubber wheel wear testing machine showed that the coating weight loss was only 0.2824 g,which was only 1/5 of the weight loss of 65 Mn matrix under the same conditions.展开更多
Induction brazecoating technology is an important means to improve the surface properties of materials.In this paper,copper plate and corundum are selected as substrates for induction brazecoating respectively.The tem...Induction brazecoating technology is an important means to improve the surface properties of materials.In this paper,copper plate and corundum are selected as substrates for induction brazecoating respectively.The temperature variation of powder and paste coating is systematically studied,and the heat conduction mode and path in the brazecoating process are analyzed.The results show that rise of the coating temperature mainly depends on the heat absorption from the substrate.The liquid-solid interface conducts heat violently and advances step by step,which promotes the melting spread of metal filler metal.The powdery brazecoating material is in a free state,and there is a gas insulation film between the powder particles and the diamond,making it difficult for substrate to conduct heat to the coating.The binder not only assists forming,shell making and oxygen isolation,but also plays an important role during melting.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.U2004186).
文摘BNi-2/WC composite wear-resisting coating was prepared on carbon steel by the method of induction brazing.The microstructure and phase composition of the composite coating were analyzed,and the bonding strength and wear-resisting performance of the coating were tested.During the process of induction brazing,the tungsten carbide partially dissolves and reacts with the filler metal alloy to form NiW compound phase,which realizes the metallurgical combination of tungsten carbide and filler metal alloy.The matrix of the filler metal alloy consists of Ni solid solution and Ni_(3)B/Ni_(3)Si eutectic phase,and the metallurgical diffusion reaction occurs between the filler metal alloy and the steel matrix.The mechanical analysis results show that the self-strength of the composite coating reaches 140 MPa and the bonding strength of the filler metal alloy to the steel matrix reaches 360 MPa.The dry sand rubber wheel wear testing machine showed that the coating weight loss was only 0.2824 g,which was only 1/5 of the weight loss of 65 Mn matrix under the same conditions.
基金supported by the 2020 Ningbo “3315 Talent Introduction Plan” Innovative Team (C-Class)the major project of Ningbo “Scientific and Technological Innovation 2025”(Grant No.2020Z111)Science and Technology Major Project of Zhejiang Province (No.203ZP20220161)
文摘Induction brazecoating technology is an important means to improve the surface properties of materials.In this paper,copper plate and corundum are selected as substrates for induction brazecoating respectively.The temperature variation of powder and paste coating is systematically studied,and the heat conduction mode and path in the brazecoating process are analyzed.The results show that rise of the coating temperature mainly depends on the heat absorption from the substrate.The liquid-solid interface conducts heat violently and advances step by step,which promotes the melting spread of metal filler metal.The powdery brazecoating material is in a free state,and there is a gas insulation film between the powder particles and the diamond,making it difficult for substrate to conduct heat to the coating.The binder not only assists forming,shell making and oxygen isolation,but also plays an important role during melting.