Sheet samples of Mg-8Li,Mg-8Li-3Al,Mg-8Li-3AlSi and Mg-8Li-5AlSi alloys were obtained by hot rolling.Optical microscope,microhardness tester,nanoindentor,X-ray diffractometer and electrochemical analyzer were adopted ...Sheet samples of Mg-8Li,Mg-8Li-3Al,Mg-8Li-3AlSi and Mg-8Li-5AlSi alloys were obtained by hot rolling.Optical microscope,microhardness tester,nanoindentor,X-ray diffractometer and electrochemical analyzer were adopted to investigate the microstructures,micro-mechanical properties and corrosion resistance.Roller was preheated to 150°C before rolling process,and rolling reduction designed was about20% per pass with a total rolling reduction of 84%.The rolled plates were annealed at 200°C for 120 min.The tensile tests were performed at room temperature.Experimental results showed that both the strength and corrosion resistance of theα＋βdual-phase of Mg-Li alloy were significantly improved with adding Al-Si elements.The strength enhancement was attributed to the solid solution of Al into theα-Mg matrix and into theβ-Li matrix as well as to the precipitation strengthening of Mg2 Si particles.Besides,the dendrite grains ofα-Mg transformed to equiaxed ones with addition of Al into alloy Mg-Li.展开更多
The microstructure evolution and phase composition of an α+β titanium alloy, Ti-3Al-5Mo-4.5V(wt.%),have been investigated. Electron probe micro analysis(EPMA) quantitative results manifest that the stability of β p...The microstructure evolution and phase composition of an α+β titanium alloy, Ti-3Al-5Mo-4.5V(wt.%),have been investigated. Electron probe micro analysis(EPMA) quantitative results manifest that the stability of β phase decreases with increasing quenching temperature, which is influenced by the significant variation of β-stabilizing elements concentration. Detailed microstructure analysis shows that the β→ωphase transformation does occur when quenching at 750℃ and 800 ℃. The ω-reflections change from incommensurate ω-spots(750 ℃) to ideal ω-spots(800 ℃) as the β stability of the alloy decreases. Further the decrease of β phase stability encourages the formation of athermal α " martensite, which has the following orientation relationships: [111]β//[110]α",[100]p//[100]α " and [-110]p//[00-1]α" with respect to the β matrix.展开更多
Evolution of deformation mechanisms and mechanical properties of Ti-3Al-5Mo-4.5V alloy with different β phase stability have been systematically investigated. β phase stability alteration is achieved through quenchi...Evolution of deformation mechanisms and mechanical properties of Ti-3Al-5Mo-4.5V alloy with different β phase stability have been systematically investigated. β phase stability alteration is achieved through quenching temperature variation from dual α+β field(700℃) to single β field(880℃). Tensile tests at ambient temperature show that apparent yield strength of the alloy experiences an abrupt decrease followed by a significant increase from 700℃ to 880℃. Work hardening behavior is characterized by transition from the initial two-regime feature to the three-stage outlook. Concurrently, the maximum working hardening rate drops from 14000 MPa to 3000 MPa, which is concurrent with the shrinking volume fraction of primary a phase. Detailed discussion about the relationship between deformation mechanisms and β phase stability has been outlined.展开更多
基金supported by National Natural Science Foundation of China(51274149,51401143)Shanxi Scholarship Council of China(No.2014-029)
文摘Sheet samples of Mg-8Li,Mg-8Li-3Al,Mg-8Li-3AlSi and Mg-8Li-5AlSi alloys were obtained by hot rolling.Optical microscope,microhardness tester,nanoindentor,X-ray diffractometer and electrochemical analyzer were adopted to investigate the microstructures,micro-mechanical properties and corrosion resistance.Roller was preheated to 150°C before rolling process,and rolling reduction designed was about20% per pass with a total rolling reduction of 84%.The rolled plates were annealed at 200°C for 120 min.The tensile tests were performed at room temperature.Experimental results showed that both the strength and corrosion resistance of theα＋βdual-phase of Mg-Li alloy were significantly improved with adding Al-Si elements.The strength enhancement was attributed to the solid solution of Al into theα-Mg matrix and into theβ-Li matrix as well as to the precipitation strengthening of Mg2 Si particles.Besides,the dendrite grains ofα-Mg transformed to equiaxed ones with addition of Al into alloy Mg-Li.
基金supported from the National Natural Science Foundation of China(No.51401221,51622401 and 51628402)support from the Strategic Priority Research Program of the Chinese Academy of Sciences(No.XDB06050100)
文摘The microstructure evolution and phase composition of an α+β titanium alloy, Ti-3Al-5Mo-4.5V(wt.%),have been investigated. Electron probe micro analysis(EPMA) quantitative results manifest that the stability of β phase decreases with increasing quenching temperature, which is influenced by the significant variation of β-stabilizing elements concentration. Detailed microstructure analysis shows that the β→ωphase transformation does occur when quenching at 750℃ and 800 ℃. The ω-reflections change from incommensurate ω-spots(750 ℃) to ideal ω-spots(800 ℃) as the β stability of the alloy decreases. Further the decrease of β phase stability encourages the formation of athermal α " martensite, which has the following orientation relationships: [111]β//[110]α",[100]p//[100]α " and [-110]p//[00-1]α" with respect to the β matrix.
基金supported by the National Natural Science Foundation of China(No.51401221,51622401 and 51628402)the support from the Strategic Priority Research Program of the Chinese Academy of Sciences(No.XDB06050100)
文摘Evolution of deformation mechanisms and mechanical properties of Ti-3Al-5Mo-4.5V alloy with different β phase stability have been systematically investigated. β phase stability alteration is achieved through quenching temperature variation from dual α+β field(700℃) to single β field(880℃). Tensile tests at ambient temperature show that apparent yield strength of the alloy experiences an abrupt decrease followed by a significant increase from 700℃ to 880℃. Work hardening behavior is characterized by transition from the initial two-regime feature to the three-stage outlook. Concurrently, the maximum working hardening rate drops from 14000 MPa to 3000 MPa, which is concurrent with the shrinking volume fraction of primary a phase. Detailed discussion about the relationship between deformation mechanisms and β phase stability has been outlined.