MnO_x/Al_2O_3 and MnO_x/ZrO_2-Al_2O_3 catalysts were prepared by incipientwetness impregnation of Mn(CH_3COO)_2 on the corresponding supports, followed by thecharacterization using X-ray diffraction (XRD), temperature programmed reduction (TPR) and BETsurface area techniques. The result shows the BET surface area of ZrO_2-Al_2O_3 is lower than thatof Al_2O_3 due to the loading of ZrO_2. However the resulted MnO_x/ZrO_2-Al_2O_3 catalyst exhibitshigher activity for methane combustion than MnO_x/Al_2O_3, because the addition of ZrO_2 ontoAl_2O_3 is beneficial for the dispersion of Mn species and the improvement of the lattice oxygenactivity in MnO_x, subsequently the activation of methane during combustion. The optimum loading ofZr in MnO_x/ZrO_2-Al_2O_3 is in the range of 5%-10% correlated with the calcination temperatures ofcatalyst supports.
MnO_x/Al_2O_3 and MnO_x/ZrO_2-Al_2O_3 catalysts were prepared by incipientwetness impregnation of Mn(CH_3COO)_2 on the corresponding supports, followed by thecharacterization using X-ray diffraction (XRD), temperature programmed reduction (TPR) and BETsurface area techniques. The result shows the BET surface area of ZrO_2-Al_2O_3 is lower than thatof Al_2O_3 due to the loading of ZrO_2. However the resulted MnO_x/ZrO_2-Al_2O_3 catalyst exhibitshigher activity for methane combustion than MnO_x/Al_2O_3, because the addition of ZrO_2 ontoAl_2O_3 is beneficial for the dispersion of Mn species and the improvement of the lattice oxygenactivity in MnO_x, subsequently the activation of methane during combustion. The optimum loading ofZr in MnO_x/ZrO_2-Al_2O_3 is in the range of 5%-10% correlated with the calcination temperatures ofcatalyst supports.
基金
This work was financially supported by Shandong Provincial Department of Science and Technology(project number:981206403)and the State Key Laboratory of Coal Conversion at Institute of Coal Chemistry of CAS(2002-2003)