Vaporizing foil actuator welding(VFAW) was used for joining 2024-T3 and 7075-T6 aluminum alloy sheets, and the resulting joint microstructure was analyzed. 2024/7075 aluminum alloy pairs with suitable processing parameters can be prepared by using VFAW. Dynamic preform addresses the poor formability problem of target material and advantage of VFAW on dissimilar materials in some conditions. But with standoff sheet inserting in the flyer and target, 2024/7075 welded pairs gets the better weld strength, compared with flyer preformed method. The microstructure of the circular weld area of the welded joint showed a wave interface, in which a thin melt layer formed at the center and edge parts. The crystal grains near the bonding interface were remarkably elongated and refined. Therefore, the joining of the 2024/7075 pairs was facilitated through plastic forming and melting.
Vaporizing foil actuator welding(VFAW) was used for joining 2024-T3 and 7075-T6 aluminum alloy sheets, and the resulting joint microstructure was analyzed. 2024/7075 aluminum alloy pairs with suitable processing parameters can be prepared by using VFAW. Dynamic preform addresses the poor formability problem of target material and advantage of VFAW on dissimilar materials in some conditions. But with standoff sheet inserting in the flyer and target, 2024/7075 welded pairs gets the better weld strength, compared with flyer preformed method. The microstructure of the circular weld area of the welded joint showed a wave interface, in which a thin melt layer formed at the center and edge parts. The crystal grains near the bonding interface were remarkably elongated and refined. Therefore, the joining of the 2024/7075 pairs was facilitated through plastic forming and melting.
基金
Funded by the State Key Laboratory of Advanced Design and Manufacturing for Vehicle Body(No.31815008)
the National Natural Science Foundation of China(No.U1564202,NO.51205298)
111 Project(No.B17034)