摘要
Binary Al-4Mg alloy have been deformed by hot torsion at 300-500 deg C andstrain rates of 0.006-1.587 s^(-1) to a true strain of 5.5. The specimens were annealed in vacuumfor 1.5 h at 500 deg C and then water quenched. The study indicates that the dynamicrecrystallization occurs during hot torsion of Al-4Mg alloy in a certain range of Z parameter(Zener-Hollmon Parameter), i.e. 19.3 <= lnZ <=24.8. Increasing the strain rate at higher deformationtemperature or reducing the strain rate at lower deformation temperature accelerates the occurrenceof dynamic recrystallization in the alloy.
Binary Al-4Mg alloy have been deformed by hot torsion at 300-500 deg C andstrain rates of 0.006-1.587 s^(-1) to a true strain of 5.5. The specimens were annealed in vacuumfor 1.5 h at 500 deg C and then water quenched. The study indicates that the dynamicrecrystallization occurs during hot torsion of Al-4Mg alloy in a certain range of Z parameter(Zener-Hollmon Parameter), i.e. 19.3 <= lnZ <=24.8. Increasing the strain rate at higher deformationtemperature or reducing the strain rate at lower deformation temperature accelerates the occurrenceof dynamic recrystallization in the alloy.
基金
The project was sponsored by the Education Administration Major Project for Science Research under the contract No. 99134.