Two new types of electrically-assisted forming(EAF) processes of AZ31B magnesium alloy sheets,i.e., electrically-assisted blanking(EAB) and electrically-assisted sheet upset-extruding(EASUE), are proposed in this paper. During EAB, pulsed current(PC) decreases blanking load and improves blanked surface quality,and higher frequency has a more effective improvement;when the frequency reaches 600 Hz, the whole punched hole fracture is improved to smooth zone. Moreover, EAB does not influence the microstructure and does not induce obvious annealing, and this process is advantageous to the materials that cannot change microstructure.During EASUE, PC can reduce extrusion load and enhance extrusion height, and higher frequency also has a more effective improvement. Both processes indicate that introducing PC can effectively improve the part quality and have an application prospection.
Two new types of electrically-assisted forming(EAF) processes of AZ31B magnesium alloy sheets,i.e., electrically-assisted blanking(EAB) and electrically-assisted sheet upset-extruding(EASUE), are proposed in this paper. During EAB, pulsed current(PC) decreases blanking load and improves blanked surface quality,and higher frequency has a more effective improvement; when the frequency reaches 600 Hz, the whole punched hole fracture is improved to smooth zone. Moreover, EAB does not influence the microstructure and does not induce obvious annealing, and this process is advantageous to the materials that cannot change microstructure.During EASUE, PC can reduce extrusion load and enhance extrusion height, and higher frequency also has a more effective improvement. Both processes indicate that introducing PC can effectively improve the part quality and have an application prospection.
基金
the National Natural Science Foundation of China(No.51635005)