Polybutadiene(PB)/Montmorillonite(MMT) nanocomposites were prepared by in situ polymerization through anionic polymerization technique.The structure of the nanocomposites was characterized by using XRD and H\|NMR.XRD results showed that the crystalline spacing in clay was increased,indicating the intercalation of PB chains in MMT crystallites, and both intercalated and exfoliated nanocomposites were prepared.From the H NMR spectra of PB and PB/MMT nanocomposites,it could be seen that the microstucture of PB was influenced by MMT.The 1,2 units content of PB molecules increased with the introduction of MMT.The dynamic properties of nanocomposites were measured by DMA.The results showed that T g and storage modulus were increased ,tan δ was decreased with MMT added,indicating that MMT has strong interaction with PB so as to reduce the friction among the chains of PB.The results of TGA revealed that the nanocomposites have better thermal stability than PB.
Polybutadiene(PB)/Montmorillonite(MMT) nanocomposites were prepared by in situ polymerization through anionic polymerization technique.The structure of the nanocomposites was characterized by using XRD and H\|NMR.XRD results showed that the crystalline spacing in clay was increased,indicating the intercalation of PB chains in MMT crystallites, and both intercalated and exfoliated nanocomposites were prepared.From the H NMR spectra of PB and PB/MMT nanocomposites,it could be seen that the microstucture of PB was influenced by MMT.The 1,2 units content of PB molecules increased with the introduction of MMT.The dynamic properties of nanocomposites were measured by DMA.The results showed that T g and storage modulus were increased ,tan δ was decreased with MMT added,indicating that MMT has strong interaction with PB so as to reduce the friction among the chains of PB.The results of TGA revealed that the nanocomposites have better thermal stability than PB.
出处
《高分子学报》
SCIE
CAS
CSCD
北大核心
2003年第4期595-598,共4页
Acta Polymerica Sinica