The 430 ℃ isothermal section of the Al 4Mg Sc Zr quaternary system in the Al rich range was determined by means of equilibrium alloys with the use of microstructure, X ray diffraction analysis and electron probe microanalysis. There coexist three single phase fields, two two phase fields and one three phase field. It is established that the phase Al 3Sc 10.5 Zr 00.5 with L1 2 structure and Al 3Zr 10.8 Sc 00.2 with DO 23 structure are in equilibrium with the α solid solution, Zr being dissolved in Al 3Sc, further substituting for about 50% Sc(mole fraction) whilst Sc is present in the phase Al 3Zr and the maximum substitution for Zr is about 20%.
The 430 ℃ isothermal section of the Al 4Mg Sc Zr quaternary system in the Al rich range was determined by means of equilibrium alloys with the use of microstructure, X ray diffraction analysis and electron probe microanalysis. There coexist three single phase fields, two two phase fields and one three phase field. It is established that the phase Al 3Sc 10.5 Zr 00.5 with L1 2 structure and Al 3Zr 10.8 Sc 00.2 with DO 23 structure are in equilibrium with the α solid solution, Zr being dissolved in Al 3Sc, further substituting for about 50% Sc(mole fraction) whilst Sc is present in the phase Al 3Zr and the maximum substitution for Zr is about 20%.
出处
《中国有色金属学会会刊：英文版》
EI
CSCD
2003年第3期546-552,共7页
Transactions of Nonferrous Metals Society of China
基金
Project(G19990 64 90 7)supportedbytheNationalKeyFundamentalResearchandDevelopmentProgramofChina