The fracture behavior for welded joint of new generation fine grained steel SS400 was investigated and assessed on the basis of fitness for purpose philosophy. The actual critical defect sizes for the SS400 base metal and its weld HAZ (heat affected zone) defined by the gross yielding criterium have been determined directly by means of wide plate tests. It has been shown that although the HAZ grain growth occurs due to the welding heat, the resistance to fracture is not deteriorated. The deformation behavior of wide plate specimen was also studied by finite, element (FE) analysis. The deformation of weld HAZ is protected by the high strength weld metal, so it is easier to get the general yielding for the welded joint specimen.
The fracture behavior for welded joint of new generation fine grained steel SS400 was investigated and assessed on the basis of fitness for purpose philosophy. The actual critical defect sizes for the SS400 base metal and its weld HAZ (heat affected zone) defined by the gross yielding criterium have been determined directly by means of wide plate tests. It has been shown that although the HAZ grain growth occurs due to the welding heat, the resistance to fracture is not deteriorated. The deformation behavior of wide plate specimen was also studied by finite, element (FE) analysis. The deformation of weld HAZ is protected by the high strength weld metal, so it is easier to get the general yielding for the welded joint specimen.
基金
Supported by FOK YING TUNG Education Foundation and the National Natural Science Foundation of China (Grant No.50275107).