摘要
为了实现降低金刚石涂层粗糙度的目的,本文研究了飞秒激光功率,重复频率以及扫描速度对金刚石涂层表面粗糙度的影响,试验之后利用白光干涉仪检测抛光区域形貌以及粗糙度。试验结果表明:粗糙度随着功率的降低而减小,当功率降至100mw以下时抛光后的粗糙度会随着功率的降低而略微的提高;重复频率对抛光后的粗糙度无显著影响;粗糙度随扫描速度的增大而减小,当扫描速度增加到1.6mm/s之后,粗糙度会出现略微的升高。在功率100mw,重复频率1KHz,扫描速度1.6mm/s的条件下,得到的粗糙度最低,约为0.14μm,局部区域粗糙度可降至100nm以下,并且抛光的区域相对于未抛光区域更具有致密性,基本上满足金刚石涂层低摩擦表面的要求。
In this study,the effects of femtosecond laser power,repetitive frequency,and scanning speed on diamond roughness were examined for the purpose of diamond coating surface Ra improvements.The morphology and roughness of fs-laser polished regions were analyzed with white-light interferometry.The experimental results showed that the diamond coating roughness decreased if the laser power decreased,and when the laser power was less than 100 mW,the roughness increased slightly with the reduced power.The laser repetitive frequency did not exhibit deteriorative effects on the roughness.The roughness decreased with decreasing scanning speed;however,a slight increase in the surface roughness was observed when the scanning velocity increased to 1.6 mm/s.Finally,under the conditions of 100 mW laser power,1 KHz repetition rate,and 1.6 mm/s scanning speed,a minimum surface roughness of approximately 0.14μm was obtained,reaching as low as 100 nm in certain local areas.Furthermore,the polished region had a higher compactness compared to the unpolished areas,and it met the requirements for low friction diamond coatings.
作者
马玉平
张遥
魏超
李翔
MA Yu-ping;ZHANG Yao;WEI Chao;LI Xiang(School of Mechanical and Electrical Engineer Anhui Jianzhu University,Hefei 230601,China)
出处
《光学精密工程》
EI
CAS
CSCD
北大核心
2019年第1期164-171,共8页
Optics and Precision Engineering
基金
国家自然基金资助项目(No.51375011)
安徽省自然科学基金资助项目(No.1208085ME63)
安徽省教育厅自然科学基金资助项目(No.KJ2015A050
No.KJ2015A013)
关键词
飞秒激光
金刚石涂层
粗糙度
致密性
femtosecond laser
diamond coating
roughness
compactness