基于贻贝仿生粘合剂多巴胺(Dopamine,DA)和聚乙烯亚胺(Polyethyleneimine,PEI)共沉积制备了阳离子交换膜并使用红外光谱仪、扫描电子显微镜和紫外可见分光光度计等手段表征其性能,研究了DA与PEI浓度比对改性膜性能的影响。结果表明,随着PEI浓度的提高改性膜的选择透过性和膜电阻呈先增加后降低趋势,而改性膜的氧化百分比呈先下降后提高的趋势。DA与PEI浓度比为1∶1的改性膜其氧化百分比和膜电阻较低,含水率和离子交换容量分别为48.68%和2.49 mmol/g,选择透过性高达97.8%,比原膜提高了8.08%。
The cation exchange membrane was prepared by co-deposition of Dopamine(DA)and Polyethyleneimine(PEI)based on mussel bionic binders,and its properties were characterized by infrared spectrometer,scanning electron microscope,and UV visible spectrophotometer.The effect of DA to PEI concentration ratio on the performance of the modified membrane was studied.The results showed that with the increase of PEI concentration,the selective permeability and membrane resistance increased first and then decreased,while the oxidation percentage of the modified membrane decreased first and then increased.When the concentration ratio of DA to PEI was 1:1,the modified membrane had lower oxidation percentage and membrane resistance.Accordingly,the water content and ion exchange capacity were 48.68%and 2.49 mmol/g,respectively,and the selective permeability was up to 97.8%,that is 8.08%superior to the original membrane.
作者
周键
夏蒙玥
张航飞
刘俏君
ZHOU Jian;XIA Mengyue;ZHANG Hangfei;LIU Qiaojun(College of Environmental and Municipal Engineering,Lanzhou Jiaotong University,Lanzhou 730070,China;Ministry of Education Engineering Research Center of Water Resource Comprehensive Utilization in Cold and Arid Regions,Lanzhou 730070,China)
出处
《材料研究学报》
EI
CAS
CSCD
北大核心
2024年第8期585-592,共8页
Chinese Journal of Materials Research
基金
国家自然科学基金(52364055)
甘肃省教育厅:高校科研创新平台重大培育项目(2024CXPT-14)
兰州交通大学“天佑青年托举人才计划”基金。
关键词
有机高分子材料
离子交换膜
共沉积
高选择透过性
organic polymer materials
ion exchange membrane
co-deposition
high selective permeability