摘要
用对粘方式制备热镀锌双相钢DP980样品,用TEM表征其截面,用TEM结合电子衍射和EDS表征其界面层结构和镀锌层结构并构建其空间关系。结果表明,与DP780在退火阶段合金元素Mn的外氧化不同,DP980主要发生内氧化和Cr元素与Mn元素的竞争性氧化,界面层中较少的MnO促进热镀锌过程中的Fe-Al反应而生成了连续致密的Fe_(2)Al_(5)抑制层,抑制了镀锌阶段的Fe-Zn反应而使DP980具有较好的热镀锌性能。同时,这种结构使弥散分布在镀锌层中的η-Zn基体生成Fe3Zn10纳米晶而避免生成有较大脆性Fe-Zn相的镀层结构,使DP980保持较好的力学性能。
Hot-dip galvanized dual-phase steel DP980 samples were prepared by adhesive method,and their cross-sections were characterized by TEM.The interface layer structure and zinc coating structure were characterized by TEM combined with SAED and EDS.Then spatial morphology and composition distribution of the interfacial layer and galvanized layer was figured.The results indicated that unlike DP780,which mainly undergoes external oxidation of Mn during the annealing stage,DP980 mainly undergoes internal oxidation.Due to the presence of Cr,its oxidation competes with that of Mn.Less MnO in the interface layer may facilitate the Fe-Al reaction in the hot galvanizing process,forming a continuous and dense Fe_(2)Al_(5)inhibiting layer,which can effectively inhibit the Fe-Zn reaction in the galvanizing stage.This is the main reason why DP980 has good hot dip galvanizing performance.In addition,this structure leads to the formation of Fe3Zn10 nanocrystals dispersed in theη-Zn matrix.This can avoid the formation of a galvanized layer structure containing large size of brittle Fe-Zn phase,which is beneficial for DP980 to maintain good mechanical properties.
作者
李沅沅
梁健
熊自柳
苗斌
田秀刚
齐建军
郑士建
LI Yuanyuan;LIANG Jian;XIONG Ziliu;MIAO Bin;TIAN Xiugang;QI Jianjun;ZHENG Shijian(School of Materials Science and Engineering,Hebei University of Technology,Tianjin 300401,China;HBIS Material Technology Research Institute,Shijiazhuang 050023,China;Technical Center of Tangshan Iron and Steel Group Co.Ltd.,Tangshan 063000,China;HBIS Co.Ltd.,Shijiazhuang 050023,China)
出处
《材料研究学报》
EI
CAS
CSCD
北大核心
2024年第6期446-452,共7页
Chinese Journal of Materials Research
基金
国家自然科学基金(52101013)
河北省中央引导地方科技发展资金项目(226Z1012G)
河钢材料技术研究院合作研究项目(HG2021104,HG2021123)。
关键词
材料表面与界面
镀锌双相钢
微观结构表征
选择性氧化
界面层结构
镀锌层结构
surface and interface in the materials
galvanized dual-phase steel
microstructure characterization
selective oxidation
interface layer structure
galvanized layer structure