摘要
以1,3-双(3-氨基丙基)-1,1,3,3-四甲基二硅氧烷(AT)、正辛基三甲氧基硅烷[SiC(8)]、四甲基氢氧化铵(TMAH)、乳糖酸(LA)为原料,通过二步反应合成了乳糖酰胺改性有机硅表面活性剂SiC(8)N-LA。通过单因素试验,确定了合成中间体SiC(8)N的最佳条件为:n(AT)∶n(SiC(8))∶n(TMAH)=6.2∶1∶0.05,反应温度为90℃,反应时间为3 h。中间体SiC(8)N收率可达87.89%,所得SiC(8)N-LA结构经过FT-IR确认。SiC(8)N-LA的表面张力为39.7 mN/m,临界胶束浓度为17.5 mg/L,具有优异的润湿性能。
The lactobionamide modified silicone surfactants SiC(8)N-LA is synthesized via two-step reactions using 1,3-bis(aminopropyl)tetramethyldisiloxane(AT),n-octyltrimethoxysilane SiC(8),tetramethylammoni⁃um hydroxide(TMAH)and lactobionic acid(LA)as raw materials.Using single factor method,the optimum conditions for synthesizing SiC(8)N are as follows:n(AT)∶nSiC(8)∶n(TMAH)=6.2∶1∶0.05,reaction tempera⁃ture is 90℃and reaction time is 3 h.The yield of the intermediate SiC(8)N can reach 87.89%,and the structure of SiC(8)N-LA is confirmed by FT-IR.The surface tension of SiC(8)N-LA is 39.7 mN/m and the critical mi⁃celle concentration is 17.5 mg/L,and it has excellent wetting properties.
作者
汪志伟
廖俊杰
陈俊颖
杨鑫然
曾小君
WANG Zhiwei;LIAO Junjie;CHEN Junying;YANG Xinran;ZENG Xiaojun(School of Material Engineering,Changshu Institute of Technology,Changshu 215500,China)
出处
《印染》
CAS
北大核心
2024年第7期43-46,共4页
China Dyeing and Finishing
基金
2024年江苏省高等学校大学生创新训练计划项目(国家级)。