摘要
In combination with theoretical calculations,experiments were conducted to investigate the evolution behavior of nonmetallic inclusions(NMIs)during the manufacture of large-scale heat-resistant steel ingots using 9CrMoCoB heat-resistant steel and CaF_(2)–CaO–Al_(2)O_(3)–SiO_(2)–B_(2)O_(3)electroslag remelting(ESR)-type slag in an 80-t industrial ESR furnace.The main types of NMI in the consumable electrode comprised pure alumina,a multiphase oxide consisting of an Al_(2)O_(3)core and liquid CaO–Al_(2)O_(3)–SiO_(2)–MnO shell,and M_(23)C_(6)carbides with an MnS core.The Al_(2)O_(3)and MnS inclusions had higher precipitation temperatures than the M_(23)C_(6)-type carbide under equilibrium and nonequilibrium solidification processes.Therefore,inclusions can act as nucleation sites for carbide layer precipitation.The ESR process completely removed the liquid CaO–Al_(2)O_(3)–SiO_(2)–MnO oxide and MnS inclusion with a carbide shell,and only the Al_(2)O_(3)inclusions and Al_(2)O_(3)core with a carbide shell occupied the remelted ingot.The M_(23)C_(6)-type carbides in steel were determined as Cr_(23)C_(6)based on the analysis of transmission electron microscopy results.The substitution of Cr with W,Fe,or/and Mo in the Cr_(23)C_(6)lattice caused slight changes in the lattice parameter of the Cr_(23)C_(6)carbide.Therefore,Cr_(21.34)Fe_(1.66)C_(6),(Cr_(19)W_(4)C_(6),Cr_(18.4)Mo_(4.6)C_(6),and Cr_(16)Fe_(5)Mo_(2)C_(6)can match the fraction pattern of Cr_(23)C_(6)carbide.The Al_(2)O_(3)inclusions in the remelted ingot formed due to the reduction of CaO,SiO_(2),and MnO components in the liquid inclusion.The increased Al content in liquid steel or the higher supersaturation degree of Al_(2)O_(3)precipitation in the remelted ingot than that in the electrode can be attributed to the evaporation of CaF_(2)and the increase in CaO content in the ESR-type slag.
基金
the Korea Evaluation Institute of Industrial Technology(KEIT,No.20009956)
the Korea Institute for Advancement of Technology(KIAT,No.P0023676,HRD Program for Industrial Innovation)
funded by the Ministry of Trade,Industry and Energy(MOTIE),Korea
the Swedish Foundation for International Cooperation in Research and Higher Education(STINT)for supporting the collaboration between KTH(Sweden)and Hanyang University(Korea)。