摘要
为提高滩涂淤泥的资源化利用率,可以通过在滩涂淤泥中按一定的配合比加入由水泥、矿渣、石膏等制备的固化剂来提高其工程可利用性。探究了以水泥、矿渣、石膏为原材料的固化剂的固化效果。结果表明:根据抗压强度,确定水泥、矿渣和石膏的最优配比分别为22.5%、70.0%和7.5%;在掺入20%最优配比固化剂的情况下,固化后滩涂淤泥3、7、28 d无侧限抗压强度分别为1.51、2.03、3.37 MPa。微观分析表明,固化剂中水化产物与淤泥颗粒相互结合,提高了整体抗压强度。固化剂可以在有效提高滩涂淤泥资源化利用率的同时兼顾工程经济性。
In order to improve the resource utilization rate of mudflat sludge,the engineering availability of mudflat sludge can be improved by adding a curing agent prepared by cement,slag,gypsum,etc.according to a certain mix proportion.Explored the solidification effect of curing agents using cement,slag,and gypsum as raw materials.The results indicated that the solidification agent with the optimal mechanical performance contains a cement-slag-gypsum ratio of 22.5%-70%-7.5%.In the case of 20%optimal solidification agent,the unconfined compressive strength of beach silt after curing for 3 days,7 days and 28 days is 1.51 MPa,2.03 MPa and 3.37 MPa,respectively.Micro-analysis result shows that the hydration products in the solidification agent are combined with silt particles to improve the overall compressive strength.Moreover,solidification agent can effectively improve the engineering availability of beach silt and take into account the engineering economy at the same time.
作者
许大鹏
练文文
屈丹妮
巴明芳
房小梁
XU Dapeng;LIAN Wenwen;QU Danni;BA Mingfang;FANG Xiaoliang(Mingyang(Ningbo)Environmental Protection Technology Co.Ltd.,Ningbo 315211,China;School of Civil&Environmental Engineering and Geography Science,Ningbo University,Ningbo 315211,China)
出处
《新型建筑材料》
2024年第4期63-67,140,共6页
New Building Materials
关键词
滩涂淤泥
固化剂
抗压强度
抗折强度
无侧限抗压强度
beach silt
solidification agent
compressive strength
flexural strength
unconfined compressive strength