摘要
针对304不锈钢氩氧脱碳(Argon-Oxygen Decarburization,AOD)精炼过程中存在炉渣成分难以测量等问题,本研究综合考虑了顶枪吹氧、供气比例变化、物料熔化速度以及初始渣量对渣-钢反应和精炼炉渣成分的影响,建立了炉渣成分预测模型,并用于计算精炼过程中的炉渣和钢液成分变化。此模型计算的渣成分与钢液硫含量与实测值吻合较好,AOD精炼终点渣中SiO_(2)含量平均偏差为1.434%,CaO含量平均偏差为1.848%,Cr_(2)O_(3)含量平均偏差为0.080%,MnO含量平均偏差为0.016%,钢液终点S含量平均偏差为0.002%。
This paper presents a model for predicting slag composition during the 304 stainless steel argon-oxygen decarburization(AOD)refining process.The model considers the effects of top gun oxygen blowing,changes in gas supply ratio,material melting rate,and initial slag amount on the slag-steel reaction and refining slag composition.It is used to calculate the refining process of slag and steel composition changes during the refining process.The slag composition and sulfur content of the molten steel,as calculated by the model,are consistent with the measured values.The average deviation for SiO_(2) content is 1.434%,for CaO content is 1.848%,for Cr_(2)O_(3) content is 0.080%,for MnO content is 0.016%,and for S content is 0.002%at the end of the AOD refining.
作者
林文志
李晶
史成斌
蔡俊
LIN Wenzhi;LI Jing;SHI Chengbin;CAI Jun(State Key Laboratory of Advanced Metallurgy,University of Science and Technology Beijing,Beijing 100083,China)
出处
《江西冶金》
2024年第2期96-105,共10页
Jiangxi Metallurgy
关键词
氩氧脱碳
304不锈钢
炉渣成分
预测模型
argon-oxygen decarburization
304 stainless steel
slag composition
prediction model