摘要
Magnesium slag(MS)is an industrial byproduct with high CO_(2)sequestration potential.This study investigates the carbonation behavior and microstructural changes of MS during wet carbonation at 0℃.XRD,TG,FTIR,SEM,and BET techniques were used to characterize the phase composition,microstructure,and porosity of MS samples carbonated for different durations.The results showed that the main carbonation products were calcite,vaterite,and highly polymerized silica gel,with particle sizes around 1μm.The low-temperature environment retarded the carbonation reaction rate and affected the morphology and crystallization of calcium carbonate.After 480 min of carbonation,the specific surface area and porosity of MS increased substantially by 740%and 144.6%,respectively,indicating improved reactivity.The microstructure of carbonated MS became denser with calcite particles surrounded by silica gel.This study demonstrates that wet carbonation of MS at 0℃significantly enhances its properties,creating an ultrafine supplementary cementitious material with considerable CO_(2)sequestration capacity.
基金
support from the National Key R&D Program Intergovernmental International Science and Technology Innovation Cooperation Project(2018YFE0107300)
the China Building Materials Federation(20221JBGS03-11)
the Science and Technology Project of Henan Province(211110231400,212102310559,212102310564,222300420167,22A430022)
the Opening Project of the State Key Laboratory of Green Building Materials(2021GBM06)
the Henan Outstanding Foreign Scientists’Workroom(GZS2021003).