摘要
Lithium(Li)metal is regarded as one of the most promising anode candidates for next-generation batteries due to its extremely high specific capacity and low redox potential.However,its application is still hindered by the uncontrolled growth of dendritic Li and huge volume fluctuation during cycles.To address these issues,flexible and self-supporting three-dimensional(3D)interlaced Ndoped carbon nanofibers(NCNFs)coated with uniformly distributed 2D ultrathin NiCo_(2)S_(4)nanosheets(denoted CNCS)were designed to eliminate the intrinsic hotspots for Li deposition.Physicochemical dual effects of CNCS arise from limited surface Li diffusivity with a higher Li affinity,leading to uniform Li nucleation and less random accumulation of Li,as confirmed by ab initio molecular dynamics simulations.Due to the unique structure,exchange current density is reduced significantly and metallic Li is further contained within the interspace between the NCNF and NiCo_(2)S_(4)nanosheets,preventing the formation of dendritic Li.The symmetric cell with a Li/CNCS composite anode shows a long-running lifespan for almost 1200 h,with an exceptionally low and stable overpotential under 1mA cm^(-2)/1 mAh cm^(-2).A full cell coupled with a LiFePO4 cathode at a low N/P ratio of 2.45 shows typical voltage profiles but more significantly enhanced performance than that of a LiFePO4 cathode coupled with a bare Li anode.
基金
Natural Sciences and Engineering Research Council of Canada,Grant/Award Numbers:Alliance‐Alberta Innovates Program/ALLRP‐561137‐20,Discovery Grant Program/RGPIN‐2020‐05184
University of Alberta Future Energy Systems。