摘要
Electrospinning is a simple technique used to fabricate polymeric nano-fibrous membranes.These nano-fibers have found a wide range of valuable applications in the biomedical field.However,it has not been utilized with solid high explosives yet.Herein,the electrospinning technique has been used to fabricate polystyrene(PS)/1,3,5-trinitro-1,3,5-triazinane(RDX)composite nanofibers.The governed electrospinning parameters,voltage,distance from the collector,flow rate,mandrel rotating speed,time,and solution concentration,that greatly affect the morphology of the obtained nanofibers were optimized.The fabricated PS/RDX nano-fibers were characterized using scanning electron microscopy(SEM),X-ray diffractometer(XRD),and Fourier Transform Infrared(FTIR)spectroscopy.The impact and friction sensitivities of PS/RDX were also measured.The thermal behavior of the prepared composite and the pure materials were studied by the thermal gravimetric analysis technique(TGA).SEM results proved the fabrication of PS/RDX fibers in the nano-size via electrospinning.FTIR spectroscopy confirmed the existence of the characteristic functional groups of both PS and RDX in the composite nano-fibers.XRD sharp peaks showed the conversion of amorphous PS into crystalline shape via electrospinning and also confirmed the formation of PS/RDX composite.The PS fibers absorbed the heat and increased the onset decomposition of the pure RDX from 181.5 to 200.7℃in the case of PS/RDX fibers.Interestingly,PS/RDX nano-fibers showed the relatively low impact and friction sensitivities of 100 J and 360 N respectively.These results could introduce PS/RDX nanofibrous composite in the field of explosives detection with high levels of safety.