The effects of fluoride ions(F^(-)) on the electrochemical behavior and coordination properties of titanium ions(Ti^(n+)) were studied in this work,by combining electrochemical and mathematical analysis as well as spectral techniques.The α was taken as a factor to indicate the molar concentration ratio of F^(-) and Ti^(n+).Cyclic voltammetry(CV),square wave voltammetry(SWV),and open circuit potential method(OCP)were used to study the electrochemical behavior of titanium ions under conditions of various α,and in-situ sampler was used to prepare molten salt samples when α equal to 0.0,1.0,2.0,3.0,4.0,5.0,6.0,and 8.0.And then,samples were analyzed by X-ray photoelectron spectroscopy(XPS) and Raman spectroscopy.The results showed that F^(-) in molten salt can reduce the reduction steps of titanium ions and greatly affects the proportion of valence titanium ions which making the high-valence titanium content increased and more stable.Ti^(2+) cannot be detected in the molten salt when α is higher than 3.0 and finally transferred to titanium ions with higher valence state.Investigation revealed that the mechanism behind those phenomenon is the coordination compounds(TiCl_(j) F_(i)^(m-)) forming.
基金
financially supported by the National Natural Science Foundation of China(No.51804277)
the State Key Laboratory of Complex Nonferrous Metal Resources Clean Utilization,China(No.CNMRCUKF2008)
the State Key Laboratory of Special Rare Metal Materials,China(No.SKL2020K004)
the Northwest Rare Metal Materials Research Institute,China。