摘要
Er_(x)Ti_(0.1)Zr_(0.9-x)O_(2-1.5 x)(x=0.04,0.05,0.06,0.07,0.08) ceramics were synthesized by a solid-state reaction method.The influence of the Er^(3+) addition on the phase composition,Vickers hardness,fracture toughness,and thermal conductivity of this ceramic material was investigated.The X-ray diffraction results reveal that the c-ZrO_(2) content increases from 1.85 vol% to 33.89 vol%,and the percentage of t-ZrO_(2) decreases from 98.15 vol% to 66.11 vol% with the increase in Er^(3+) content from 4 mol% to 8 mol%.Moreover,the addition of Er^(3+) is beneficial to the volume expansion of the unit cell.At the same time,the incorporation of Er^(3+) weakens the coordination of oxygen ions around the metal cations,resulting in a corresponding decrease in the tetragonality of the t-ZrO_(2).The Vickers hardness and fracture toughness of the Er_(x)Ti_(0.1)Zr_(0.9-x)O_(2-1.5)_(x) ceramics show increasing and decreasing trends,respectively.The thermal conductivity has a significant decline due to point defects caused by the Er^(3+) doping.The 8 ETZ ceramic exhibits the highest Vickers hardness(12.7 GPa),the lowest fracture toughness(7.6 MPa·m^(1/2)),and the lowest average thermal conductivity(1.85 W/(m·K)) in the temperature range of 200-1000℃.All of the above properties are higher than those of the Y_(2)O_(3)-stabilized ZrO_(2) ceramic.
基金
Project supported by the National High Technology Research and Development Program of China(2015AA034403)
the National Natural Science Foundation of China(Grant No.51762036)。