摘要
采用TIG焊粉末堆焊技术在Q235基体上制备了00Cr21NiMn5Mo2N双相不锈钢堆焊层。在1170℃对堆焊层试样进行固溶处理,之后在800℃分别敏化处理0.5、1、2和4 h,探究经不同时长的敏化处理后材料的组织和性能变化。显微组织观察表明,固溶处理后堆焊层组织由奥氏体(γ)和铁素体(α)两相组成。敏化处理后析出相沿相界析出,且含量随着敏化时间的延长逐渐增多。点蚀浸泡实验、动电位极化曲线测试、电化学阻抗谱测量表明,试样的耐腐蚀性能在敏化时间从0.5 h到2 h时下降;然而,敏化4 h的样品的耐腐蚀性显著提高,甚至超过固溶处理后的耐腐蚀性能。
In order to study the effect of the precipitated phase on the corrosion resistance of duplex stainless steel, surfacing layers of 00Cr21NiMn5Mo2N duplex stainless steel were prepared on Q235 via tungsten inert gas(TIG) powder surfacing. The surfacing layered samples were solid-solution treated at1170 ℃, then sensitized at 800 ℃ for 0.5, 1, 2 and 4 h respectively, and then the effect of sensitization time on the microstructure and corrosion resistance of the surfacing layer was assessed. The results showed that the microstructures of the duplex stainless steel surface layers after solution treatment were mainly composed of ferrite phase and austenite phase. After sensitization, the precipitated phase dispersed along phase boundaries, while the content of the precipitated phase gradually increased with the sensitization time. The corrosion resistance of the samples decreased when the sensitization time increased from 0.5 h to 2 h. However, the corrosion resistance of the samples sensitized for 4 h increased significantly. The pitting potential of the sample sensitized for 4 h was 668 mV higher than that of the sample sensitized for 2 h. In addition, the morphology of samples after pitting also reflected the change of pitting resistance of the samples.
作者
包晔峰
武竹雨
陈哲
郭林坡
王子睿
曹冲
宋亓宁
BAO Yefeng;WU Zhuyu;CHEN Zhe;GUO Linpo;WANG Zirui;CAO Chong;SONG Qining(College of Mechanical and Electrical Engineering,Hohai University,Changzhou 213022,China)
出处
《中国腐蚀与防护学报》
CAS
CSCD
北大核心
2022年第6期1027-1033,共7页
Journal of Chinese Society For Corrosion and Protection
基金
国家自然科学基金(51879089)。
关键词
TIG粉末堆焊
双相不锈钢
敏化处理
析出相
点蚀
TIG powder surfacing
duplex stainless steel
sensitization treatment
precipitation phase
pitting corrosion