摘要
Aiming at the process of smelting ultra-high(>80%)or even full vanadium titanomagnetite in blast furnace,we are conducting a series of works on physics character of high TiO_(2) bearing blast furnace slag(BFS)for slag optimization.This work discussed the density and surface tension of high TiO_(2) bearing BFS using the Archimedean principle and the maximum bubble pressure method,respectively.The influence of TiO_(2) content and the MgO/CaO mass ratio on the density and surface tension of CaO-SiO_(2)-TiO_(2)-MgO-Al_(2)O_(3)slags were investigated Results indicated that the density of slags decreased with the TiO_(2) content increasing from 20wt%to 30wt%,but it increased slightly with the MgO/CaO mass ratio increasing from 0.32 to 0.73.In view of silicate network structure,the density and the degree of polymerization(DOP)of network structure have a consistent trend.The addition of TiO_(2) reduced(Q^(3))^(2)/(Q^(2)) ratio(Q^(2) and Q^(3) represent structural unit with bridge oxygen number of 2 and 3,respectively)and then decreased DOP,which led to the decrease of slag density.The surface tension of CaO-SiO_(2)-TiO_(2)-MgO-Al_(2)O_(3) slags decreased dramatically with the TiO_(2) content increasing from 20wt%to 30wt%.Conversely,it increased with the MgO/CaO mass ratio increasing from 0.32 to 0.73.Furthermore,the iso-surface tension lines were obtained under 1723 K using the Tanaka developed model in view of Butler formula.It may be useful for slag optimization of ultra-high proportion(>80%)or even full vanadium titanomagnetite under BF smelting.
基金
financially supported by the National Key R&D Program of China(No.2018YFC1900500)
the Key Fund of Natural Science(No.51974048)。