摘要
A yellow emitting long afterglow luminescence material SrSc_(2)O_(4):Pr^(3+)was successfully prepared by solid state reaction method.SrSc_(2)O_(4):Pr^(3+)phosphor shows a long afterglow luminescence peak at about 495,545,621,630 and 657 nm,respectively,corresponding to the f–f transitions of Pr^(3+).The afterglow chromaticity coordinates of SrSc_(2)O_(4):1 at%Pr^(3+)were calculated to be(0.35,0.41),indicating that the afterglow emission is close to the light of yellow region.And,the afterglow luminescence of the optimal sample doped by 1 at%Pr^(3+)can persist for over 3 h.The thermoluminescence results suggest that there are three types of traps with depth of 0.61,0.69 and 0.78 eV exiting for all the samples,which are produced by the addition of Pr^(3+)ions.The trap density of SrSc_(2)O_(4):1 at%Pr^(3+)is the maximum when the incorporation of Pr^(3+)ions reaches 1 at%,which thus results in the longest afterglow luminescence.All the results indicate that SrSc_(2)O_(4):Pr^(3+)can be a potential candidate of novel long afterglow phosphors.
基金
Project supported by the National Natural Science Foundation of China(11974013,51802137)
the State Key Research Projects of Shandong Natural Science Foundation(ZR2020KB019)
the fund of"Two-Hundred Talent"plan of Yantai City
Major Basic Research Projects of Shandong Natural Science Foundation(ZR2020ZD36)。