The effect of Al content(0.035 wt%,0.5 wt%,1 wt%,and 2 wt%)on the composition change of steel and slag as well as inclusion transformation of high manganese steel after it has equilibrated with Ca O-Si O_(2)-Al_(2)O_(3)-Mg O slag was studied using the method of slag/steel reaction.The experimental results showed that as the initial content of Al increased from 0.035 wt%to 2 wt%,Al gradually replaced Mn to react with Si O_(2)in slag to avoid the loss of Mn due to the reaction;this process caused both Al_(2)O_(3)in slag and Si in steel to increase while Si O_(2)and Mn O in slag to reduce.In addition,the type of inclusions also evolved as the initial Al content increased.The evolution route of inclusions was Mn O→Mn O-Al_(2)O_(3)-Mg O→Mg O→Mn O-Ca O-Al_(2)O_(3)-Mg O and Mn O-Ca O-Mg O.The shape of inclusions evolved from spherical to irregular,became faceted,and finally transformed to spherical.The average size of inclusions presented a trend that was increasing first and then decreasing.The transformation mechanism of inclusions was explored.As the initial content of Al increased,Mg and Ca were reduced from top slag into molten steel in sequence,which consequently caused the transformation of inclusions.
基金
financially supported by the Ministry of Industry and Information Technology of China(No.TC180A6MR)
China Scholarship Council and the National Natural Science Foundation of China(No.51404020)。