基于静电纺丝技术将金属Ce掺杂到Bi_(2)O_(3)中,研究制备出了光催化活性增强的新型一维线性复合催化剂,并通过XRD、SEM、TEM、UV vis-DRS表征与分析,研究了不同掺杂比例对Bi_(2)O_(3)改性的影响,并将自制的光催化剂应用于液相中光降解甲基橙染料有机物.以甲基橙为目标降解物,研究结果表明,金属Ce成功地掺杂到Bi_(2)O_(3)中替换了部分Bi的晶格位,其中掺杂比例为0.25时获得了最佳的可见光催化活性,其吸收边红移最大,增禁带宽度为2.22eV,可见光照射下90min对MO催化降解率达到98.81%,光降解过程符合一级动学过程,光催化剂可见光催化降解有机污染物性能优良.研究结果为新型铈掺杂氧化铋复合催化材料在光催化领域内处理难生物降解污染物提供理论依据和技术支持.
The metal Ce was doped into Bi_(2)O_(3) Based on the electrospinning technology,and a novel linear composite catalyst with enhanced photocatalytic activity was prepared.The effect of different doping ratio on the modification of Bi_(2)O_(3) was studied by XRD,SEM,TEM and UV vis DRS characterization and analysis.And the home-made photocatalyst was applied to treat dye wastewater in the liquid phase,with degradation of methyl orange as the goal,the research results show that metal Ce successfully doped into the Bi_(2)O_(3)replaced the part of the Bi lttice,the doping ratio of 0.25 possess best visible light catalytic activity,the absorption edge redshift is the largest,and the band gap width is 2.22 eV,The catalytic degradation rate of MO under visible light irradiation reaches 98.81%in 90 minutes.The photodegradation process conforms to the first-order kinetic process,and the photocatalyst property is stable.The research results provide basis and support for the modification and development of Bi_(2)O_(3),the development of new composite photocatalytic materials,and the photodegradation of organic pollutants with poor biodegradability in the water treatment field.
作者
包海峰
欧阳文璟
严雨阳
郑雨莹
BAO Haifeng;UYANG Wenjing;YAN Yuyang;ZHENG Yuying(School of Resources and Environment Engineering,JiLin University of Chemical Technology,Jilin 132022,China)
出处
《吉林化工学院学报》
CAS
2021年第11期71-79,共9页
Journal of Jilin Institute of Chemical Technology
关键词
光催化
可见光
掺杂
静电纺丝
甲基橙染料
photocatalysis
visible light
doping
electrospinning
methyl orange dye