摘要
制备Au@Cu_(2)O核壳纳米材料与石墨烯,用于玻碳电极的修饰,构建了阿魏酸电化学传感器(Au@Cu_(2)O/Gr/GCE),利用透射电子显微镜表征修饰材料的形貌特征,采用循环伏安法(CV)和差分脉冲伏安法(DPV)研究阿魏酸在该修饰电极上的电化学行为。结果表明,该修饰电极对阿魏酸具有很好的电催化作用。在最佳实验条件下,阿魏酸的峰电流与浓度在2.5×10^(-6)~1.5×10^(-4) mol/L内具有良好的线性关系,线性相关系数为0.9932,检测限为1.2×10^(-6) mol/L。实验结果表明,Au@Cu_(2)O/Gr修饰电极具有良好的选择性、稳定性和较高灵敏度。
An electrochemical sensor for ferulic acid is developed by preparing Au@Cu_(2)O Core-shell nanomaterials and graphene modified glassy carbon electrode(Au@Cu_(2)O/Gr/GCE).Transmission electron microscope(TEM)was used to characterize the morphologies of the nanomaterials,while cyclic voltammetry(CV)and differential pulse voltammetry(DPV)were used to investigate the electrochemical behavior of ferulic acid.The modified electrode performs effective electrocatalysis to the ferulic acid.Under optimum conditions,the peak current of ferulic acid has a good linear relationship with the concentration in the range of 2.5×10^(-6)−1.5×10^(-4) mol/L,with a detection limit of 1.2×10^(-6) mol/L,the corelation coefficient 0.9932.The results show that Au@Cu_(2)O/Gr/GCE exhibits good selectivity,stability and higher sensitivity.
作者
朱丽云
黄连英
罗敏怡
石慧玲
肖世秀
冯军
ZHU Liyun;HUANG Lianying;LUO Minyi;SHI Huiling;XIAO Shixiu;FENG Jun(Medical School,Guangxi University of Science and Technology,Liuzhou 545005,China)
出处
《广西科技大学学报》
2022年第1期33-38,45,共7页
Journal of Guangxi University of Science and Technology
基金
广西高校中青年教师科研基础能力提升项目(2020KY08009)
广西大学生创新创业训练计划项目(201910594207)
广西自然科学基金项目(2016GXNSFAA380108)
广西科技大学科学基金项目(校科自174513)资助。