Disordered-structure crystals have drawn increasing attention as promising ultrashort laser material hosts owing to their broad linewidth.Herein,a novel disordered Nd:YSr_(3)(PO_(4))_(3)(Nd:YSP)crystal with good quality was successfully grown via the Czochralski pulling technique.The absorption and fluorescence spectra of the Nd:YSP single crystal were recorded at ambient temperature.The maximum absorption cross section for Nd:YSP single crystal is found to be approximately 3.89×10^(-20) cm^(2).The stimulated emission cross section for Nd:YSP crystal at~1060 nm was determined to be 7.64×10^(20) cm^(2) with the full width half maximum value of 22 nm.The fluorescence lifetime of the Nd3+ions in the Nd:YSP crystal is fitted to be 288μs.Diode-pumped continuous-wave laser operation is firstly realized at approximately 1060 nm.The maximum output power value from the Nd:YSP crystal is 714 mW,corresponding to a slope efficiency of-12.8%.The results indicate that the Nd:YSP crystal with a disordered structure may be a promising disordered laser host.
基金
Project supported by the National Natural Science Foundation of China(51872165)
the Primary Research&Development Plan of Shandong Province(2019JZZY010313)。