Herein,isotactic polypropylene films with smallβ-nucleating agent content were fabricated via a melt-extrusion-stretched technology with intended"shear-free"in barrel and die.Compared with neat films,the tensile strength,elongation at break and strain energy density at break of i PP film with 0.05 wt%β-nucleating agent are significantly improved by 13.8%,39.6%and 90.6%,respectively,indicating the simultaneously enhanced toughness and strength.Additionally,theβ-crystal content gradually increases with increasingβ-NA content,while the relative total daughter content ofα-andβ-crystal exhibits opposite tendency.Moreover,nucleation and crystal growth induced by variousβ-NA contents are different.This work proves an efficient strategy to enhance mechanical properties of isotactic polypropylene film via controlling elongation flow and addition of appropriateβ-NA content.