摘要
Nd0.7 Sr0.3MnO3 ceramics with secondary phases were prepared by ball-milling and post heat- treatment at 1623 K for 3,7 and 13h,respectively.The results from x-ray diffraction and energy dispersed spectroscopy show that some secondary phases are introduced and grow gradually with sintering time.These secondary phases have significant effects on the ac transport.For all the samples,the real part of impedance (Zr) decreases with increasing frequency and the Zr peak moves to a higher temperature.Interestingly,for a given frequency the Zr peak decreases with sintering time.However,for samples B and C which were sintered for a longer time than sample A,an additional Zr peak appears at a higher temperature and gradually increases with sintering time.The reposition of trapped charges in phase/grain boundaries or secondary phases is supposed to be responsible for the unusual relaxation process.
作者
CHEN Shun-Sheng
YANG Chang-Ping
LUO Xiao-Jing
Medvedeva I V
陈顺生;杨昌平;罗晓婧;Medvedeva I V(School of Mathematics and Physics,Hubei Polytechnic University,Huangshi 435003;Faculty of Physics and Electronic Technology,Hubei University,Wuhan 430062;Institute of Metal Physics,Ural Division of the Russian Academy of Sciences,Ekaterinburg 620219)
基金
Supported by the Program for New Century Excellent Talents in University under Grant No NCET-08-0674.