摘要
Porous structures are highly preferred for bone regeneration and high tissue in-growth.In present work,electrical discharge drilling(EDD),a thermal erosion process was used to produce through holes in Mg-alloys to fabricate perforated structure similar to open cell porous structure in extruded AZ31.Apatite formation and weight loss study was conducted for 7 days,14 days and 21 days after immersion tests in SBF solution.The perforated structure in AZ31 with 26 through micro-holes provides 72%increase in surface area but with marginally 4%higher weight loss as compare to non-perforated structure.Comparing perforated and non-perforated samples of Mg-alloy,it was well observed that perforated structure forms high volume of apatite as compared to non-perforated structure.Scanning electron microscopic(SEM)study revealed that in perforated structure,drilled holes retain their circularity after 21 days of immersion test and distinct corrosion phenomenon occur at localized sites.