This paper investigated the corrosion behaviors of Ti_(3)AlC_(2) at 700℃in molten KOH with various mass ratios.If the mass ratio of KOH:Ti_(3)AlC_(2)≤2,Ti_(3)AlC_(2) can resist KOH hot corrosion in 2 h.Ti_(3)AlC_(2) suffered serious corrosion attack if the mass ratio≥3.The main compositions of corroded samples were amorphous graphite and potassium titanates(K_(2)O·nTiO_(2)).If the samples were washed by acid and dried,potassium titanates could decompose to K_(2)O and amorphous rutile.Based on the experimental results,a corrosion mechanism of Ti_(3)AlC_(2) in molten KOH was proposed.