摘要
分析了酒钢线棒作业区棒材(HRB400)在粗轧过程中产生的头部开裂(劈头)产生的原因,就钢水成分控制、优化连铸过程、加钒铁后的热处理、加热炉温度以及粗轧出现劈头的紧急处理等方面提出了应注意问题以及解决方案。
This paper analyzes the rod of high speed wire rod at JICCO(HRB400) causes of head cracking during rough rolling, control of composition of molten steel,optimization of continuous casting process,heat treatment after ferro-vanadium,problems should be paid attention to in heating furnace temperature and emergency treatment of rough rolling and the possible solution is put forward.