摘要
The properties of activated coke(AC)for sintering flue gas purification greatly affect the efficiency of desulfurization and denitration,but they gradually change during cycles.The change in properties of coal-based AC during cycles was studied to clarify the change law and AC optimization index.The AC oxygen content rapidly increases 13.49 to 17.87 wt.%in the early cycles to form phenol,which promotes the denitration rate 55.63%to 78.20%.The denitration performance slowly increases in subsequent cycles becaof the generation of quinone AC slow oxidation.However,the oxygen-containing groups are not conducive to adsorption capacity of AC for NO.The adsorbed NO species which can be replaced SO2 is the main NO species on AC,and its amount decreases with the decrease in CC content of AC.The AC chemical loss leads to the opening of closed pores,expansion of original pores and formation of new pores,causing micropore volume to increase 0.085%to 0.152%,compressive strength to decrease 472 to 336 N,and abrasive resistance to decrease 97.87%to 94.16%during cycles.The low oxygen content and high micropore volume are favorable to the initial desulfurization performance,and the former is more decisive.After a while,the desulfurization rate is linearly positively correlated with the micropore volume regardless of the chemistry.4-h desulfurization rate increased 69.03%to 85.91%during 25 cycles due to the increasing micropore volume.The AC properties change in cycles will greatly affect the desulfurization and denitration rate in the height direction of the flue gas purification system.Selecting the coal-based AC with moderate micropore volume,easy oxidation surface and less original oxygen-containing groups facilitates the better purification efficiency at lower cost for sintering plants.
基金
the financial support of Fundamental Research Funds for the Central Universities(Grant No.FRF-IC-18-010).