Effect of vanadium addition on microstructure and properties of AI_(0.5)Cr_(0.9)FeNi_(2.5)multi-principal alloys 被引量:1

原文传递
导出
摘要 AI_(0.5)Cr_(0.9)FeNi_(2.5)V_(x)(x=0,0.2,0.4,0.6,0.8,1.0)multi-principal alloys were prepared by vacuum arc melting.The effect of vanadium addition on its microstructure and properties was investigated.The results show that the alloys of all components exhibited an FCC single-phase structure.With the addition of vanadium,the microstructure of the alloy changed from dendrites to equiaxed crystals,the grains were remarkably refined,and the layered CrV phase was exhibited,which improved the properties of the alloy.The yield strength of the alloy was slightly improved,and the alloys with various components presented good plasticity.When V content reached 0.8,the yield strength was 600 MPa,and no fracture occurred.Friction-wear testing showed that the wear debris was reduced with the addition of V element.The sample with V element content of 0.4 had the best friction and wear performance.The surface grooves became shallow,the worn debris was less,and the wear mechanism was mainly abrasive wear.The polarisation curve showed that the alloy with V element content of 0.2 has the best corrosion resistance.The passivation interval reached 900 mV.The corrosion potential and the corrosion current density were-496.299 mV and 2.759μA/cm^(2),respectively.
出处 《Journal of Iron and Steel Research International》 SCIE EI CSCD 2021年第5期586-596,共11页
基金 This work was financially supported by the Natural Science Foundation of Liaoning Province(No.2019-MS-247) the Liaoning Revitalization Talents Program(XLYC1807178) Scientific Research Project of Liaoning Provincial Department of Education(LJGD2019002).
  • 相关文献

参考文献1

共引文献22

同被引文献11

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部