以2-丙烯酰胺基-2-甲基丙磺酸(AMPS)、丙烯酸(AA)、瓜尔胶(GG)为原料,N,N-亚甲基双丙烯酰胺(NMBA)为交联剂,通过超声辐射合成AMPS/AA/GG三元共聚树脂,借助热重曲线(TG)对树脂的热降解特性进行分析。实验结果表明:在优化条件下,树脂的吸水率最大,而且树脂具有良好的耐热性能和保水性能;热分解动力学分析结果显示树脂热降解活化能为164.29 kJ/mol,lg A为13.84,反应级数n=1/6,树脂的热降解遵循44号随机成核和随后生长机理。
Using 2-acrylamide-2-methylpropionic sulfonic acid(AMPS),acrylic acid(AA)and guar gum(GG)as raw materials,N,N-methyl bisacrylamide(NMBA)as crosslinking agent,a copolymer resin of AMPS/AA/GG was prepared by ultrasonic irradiation polymerization and the corresponding thermal degradation behavior was also studied by TG.The results showed that under the optimized condition,the water absorbency of the resin was the largest and the resin had an excellent thermal stability and good retention ability.The activation energy,lg A and reaction order n were 164.29 kJ/mol,13.84 and 1/6 respectively by kinetics methods and the thermal degradation process followed the random nucleation and subsequent growth mechanism.
作者
谭德新
袁敏慧
廖湘庆
郭慧琼
梁月荣
李宇宁
TAN Dexin;YUAN Minhui;LIAO Xiangqing;GUO Huiqiong;LIANG Yuerong;LI Yuning(School of Chemistry and Chemical Engineering,Lingnan Normal University,Zhanjiang Guangdong 524048,China)
出处
《包装学报》
2021年第1期15-21,68,共8页
Packaging Journal
基金
广东省科技创新战略专项资金资助项目(2018A01005)。
关键词
树脂
吸水率
热降解
活化能
resin
water absorbency
thermal decomposition
activation energy