摘要
采用实验室化学浸泡、电化学腐蚀试验及维氏硬度测量技术研究了DSS2205爆炸及热轧复合板复层性能,利用金相显微镜、透射电镜分析了复层组织,并与复合前的DSS2205进行了对比分析。结果表明:相比复合前的DSS2205不锈钢,轧制和爆炸复合板复层腐蚀性能略有下降,硬度增加,但轧制复合板复层腐蚀性能优于爆炸复合板复层;轧制复合板复层组织为棒状奥氏体不完全呈一条直线分布于铁素体上,奥氏体发生再结晶;爆炸复合板复层仍为复合前的奥氏体和铁素体间隔分布带状组织,铁素体和奥氏体均出现变形。
The properties of composite layer of DSS2205 rolled and exploded clad plates were studied by means of chemical immersion in laboratory,electrochemical corrosion test and Vickers hardness measurement. The microstructure was analyzed by metallographic microscope and transmission electron microscope,which was compared with DSS2205 stainless steel before cladding. The results showed that the corrosion properties of composite layer of rolled and exploded clad plate were slightly decreased and the hardness was increased compared with DSS2205 stainless steel before cladding. But the corrosion properties of composite layer of the rolled clad plates were better than those of explosion clad plates. The microstructure of the composite layer of rolled clad plates was composed of rodlike austenite,which was not distributed in a straight line on the ferrite,and the austenite had recrystallization. Meanwhile,the microstructure of composite layer of the explosion clad plates was still composed of band structure with interval distribution of austenite and ferrite before cladding. The both ferrite and austenite were deformed.
作者
张欣耀
查小琴
任永峰
张文利
罗先甫
刘晓勇
ZHANG Xinyao;ZHA Xiaoqin;REN Yongfeng;ZHANG Wenli;LUO Xianfu;LIU Xiaoyong(Luoyang Ship Material Research Institute,Luoyang 471023,China;Henan Key Laboratory of Technology and Application of Structural Materials for Ships and Marine Equipments,Luoyang 471023,China;School of Materials Science and Engineering,Henan University of Science and Technology,Luoyang 471023,China)
出处
《物理测试》
CAS
2021年第1期1-5,共5页
Physics Examination and Testing
基金
国家重点研发计划资助项目(2016YFC0401205)。
关键词
2205双相不锈钢复合板
腐蚀性能
力学性能
微观组织
2205 duplex stainless steel cladded plate
corrosion property
mechanical property
microstructure