摘要
The binder properties were determined in accordance with Chinese standard such as ductility test, which allowed to measure the distance in centimeters that a standard briquette of asphalt had been stretched before breaking. Then, penetration test was carried out in order to know some properties of the asphalt, which are the hardness and the softness. Finally, softening point test was carried out in order to determine the temperature at which the bitumen attains a particular degree of softening under the specification of the test. According to Chinese standard for performance tests, firstly, Marshall test was carried out in order to measure the theoretical density, air voids, voids filled with asphalt, stability, flow, and voids in mineral aggregate of asphalt specimens. Secondly, Freeze-thaw splitting test was carried out in order to determine Splitting strength ratio. Finally, dynamic stability (rutting) test was carried out to determine average dynamic stability. Beside the tests carried out, the gradation of the extracted aggregate in accordance with American Association of State Highway and Transportation Officials was carried out to determine the dimensions of the particles weight distribution. Furthermore, both the percentage of recycled asphalt pavement materials and binder in mixture were determined to know how much of the new material during the mixture was needed. However, two specimens were used to evaluate the performance of recycled asphalt pavement materials. One specimen of recycled asphalt pavement materials was ten years old, and another one of recycled asphalt pavement materials was five years old. The results show that the conditions of the environment such as moisture, temperature, and age, decrease the ductility and penetration properties of binder when increase the softening point property of binder. Then the gradation of recycled asphalt pavement aggregate is of the required values to reuse in the mixture, while the flow ratio, the splitting strength ratio, and the dynamic stability ratio,
基金
Funded by the Technology Research and Development Plan Program of Heilongjiang Province(No.GA19A501)。