The corrosion behavior of 304 stainless steel(SS)in the presence of aerobic halophilic archaea Natronorubrum tibetense was investigated.After 14 days of immersion,no obvious pitting pit was observed on the SS surface in the sterile medium.By contrast,the SS exhibited serious pitting corrosion with the largest pit depth of 5.0μm in the inoculated medium after 14 days.The results of electrochemical tests showed that the barrier property of the passive film decreased faster in the inoculated medium.The X-ray photoelectron spectroscopy results indicated that the detrimental Fe2+and Cr6+increased in the passive film under the influence of archaea N.tibetense,which resulted in the accelerated deterioration of passive film and promoted the pitting corrosion.Combined with the energy starvation tests,the microbiologically influenced corrosion mechanism of 304 SS caused by halophilic archaea N.tibetense was discussed finally.
基金
the Beijing Nova Program(No.Z171100001117076)
the National Natural Science Foundation of China(Nos.51871026,51771029)
the National Environmental Corrosion Platform。