Functional carbonaceous materials for supercapacitors(SCs)without using acid for post-treatment remain a substantial challenge.In this paper,we present a less harmful strategy for preparing three-dimensional(3D)N,O-codoped egg-box-like carbons(EBCs).The as-prepared EBCs with opened pores provide plentiful channels for ion fast transport,ensure the e ective contact of EBCs electrodes and electrolytes,and enhance the electron conduction.The nitrogen and oxygen atoms doped in EBCs improve the surface wettability of EBC electrodes and provide the pseudocapacitance.Consequently,the EBCs display a prominent areal capacitance of 39.8μF cm-2(340 F g-1)at 0.106 m A cm-2 in 6 M KOH electrolyte.The EBC-based symmetric SC manifests a high areal capacitance to 27.6μF cm-2(236 F g-1)at 0.1075 m A cm-2,a good rate capability of 18.8μF cm-2(160 F g-1)at 215 m A cm-2 and a long-term cycle stability with only 1.9%decay after 50,000 cycles in aqueous electrolyte.Impressively,even in all-solid-state SC,EBC electrode shows a high areal capacitance of 25.0μF cm-2(214 F g-1)and energy density of 0.0233 m Wh cm-2.This work provides an acid-free process to prepare electrode materials from industrial by-products for advanced energy storage devices.
基金
the funding support of this work by the National Natural Science Foundation of China(Nos.U1710116,U1508201 and 51872005).